PPA AF-1145 V0 SOLVAY USA
AMODEL®
Automotive components、Sports equipment、Vehicle electronics、Industrial components、Shell、Parts under the hood of a、Power/Other Tools、Metal substitution、Valves/valve components、Industrial applications、Machine/mechanical compon、Laptop case、Application in the automo
High temperature resistan、Flame retardant、Thermal stability、Filler: Glass fiber reinf、45% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SOLVAY USA/AF-1145 V0 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23℃ | kJ/m² | 4.178to19.964 |
| hardness | Test Condition | Test Method | SOLVAY USA/AF-1145 V0 |
|---|---|---|---|
| Rockwell hardness | 23℃ | 125 |
| Mechanical properties | Test Condition | Test Method | SOLVAY USA/AF-1145 V0 |
|---|---|---|---|
| Yield, 23 ℃ | 12.62to270.34 MPa | ||
| shear strength | 23℃ | 88.28to107.59 MPa | |
| Yield, 23 ℃ | % | 1.5to2.6 | |
| Tensile modulus | 摩擦系数 | 0.15to0.52 | |
| Fracture, 23 ℃ | 108.28to262.76 MPa | ||
| Poisson's ratio | 23℃ | 0.41 | |
| Fracture, 23 ℃ | % | 1.0to2.5 | |
| compressive strength | 23℃ | 142.76to196.55 MPa |
| Electrical performance | Test Condition | Test Method | SOLVAY USA/AF-1145 V0 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | V | ||
| CTI | V |
| flammability | Test Condition | Test Method | SOLVAY USA/AF-1145 V0 |
|---|---|---|---|
| Limiting Oxygen Index | % | 23to25 | |
| Hot filament ignition temperature | °C | 721to926 | |
| Burning wire flammability index | °C | 743to960 |
| physical property | Test Condition | Test Method | SOLVAY USA/AF-1145 V0 |
|---|---|---|---|
| Balance, 23 ℃, 50% RH | % | 0.21to1.2 | |
| Flow: 23 ℃ | 流动,23℃ | mm/mm | 48.3E-3-129.5E-3 |
| 23℃,24hr | % | 0.12to0.30 | |
| Lateral flow: 23 ℃ | 横向, 23℃ | mm/mm | 119.4E-3-0.254 |
| Thermal performance | Test Condition | Test Method | SOLVAY USA/AF-1145 V0 |
|---|---|---|---|
| 8.0Mpa, Not annealed | °C | 165to230 | |
| vicat | °C | 258to313 | |
| Continuous use temperature | °C | 140to186 | |
| 0.45MPa, annealing | °C | 296to320 | |
| flow | mm/mm/°C | 185.4E-5-25.4E-5 | |
| 0.45MPa, Not annealed | °C | 273to312 | |
| RTI | °C | 119to150 | |
| RTI Imp | °C | 118to150 | |
| 1.8MPa, annealing | °C | 283to300 | |
| RTI Elec | °C | 140to150 | |
| 1.8MPa, Not annealed | °C | 249to304 | |
| horizontal | mm/mm/°C | 63.5E-5-177.8E-5 |