Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS+PBT LONGLITE® PBT 7330H-104 Chang Chun Plastics Co., Ltd. (CCP Group)
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Test Condition | Test Method | Chang Chun Plastics Co., Ltd. (CCP Group)/LONGLITE® PBT 7330H-104 | |
|---|---|---|---|
| Tensile modulus | 23°C | ISO 527-2 | 8200 MPa |
| Flexural modulus | 23°C | ISO 178 | 6000 MPa |
| Shrinkage rate | MD | ISO 294-4 | 0.10to0.30 % |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 10 kJ/m² |
| Volume resistivity | IEC 60093 | 1E+14 ohms·cm | |
| bending strength | 23°C | ISO 178 | 140 MPa |
| density | ISO 1183 | 1.40 g/cm³ | |
| melting temperature | ISO 11357-3 | 225 °C | |
| Shrinkage rate | TD | ISO 294-4 | 0.50to1.1 % |
| dielectric strength | 2.00mm | IEC 60243-1 | 23 kV/mm |
| Surface Resistivity | IEC 60093 | 1E+13 ohms | |
| UL flame retardant rating | UL 94 | HB | |
| Tensile strain | 断裂,23°C | ISO 527-2 | 2.4 % |
| melt viscosity | 260°C | ISO 11443 | 220 Pa·s |
| tensile strength | 断裂,23°C | ISO 527-2 | 100 MPa |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 160 °C |