ABS 3453 TRINSEO HK
--
--
High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | TRINSEO HK/3453 |
|---|---|---|---|
| Tensile modulus | 3.20mm,注塑 | ISO 527-2 | 2280 Mpa |
| Flexural modulus | 3.20mm,InjectionMolded | ISO 178 | 2300 Mpa |
| bending strength | 3.20mm,InjectionMolded | ISO 178 | 68.0 Mpa |
| tensile strength | Yield,3.20mm,InjectionMolded | ISO 527-2/50 | 45.0 Mpa |
| Tensile strain | Yield,3.20mm,InjectionMolded | ISO 527-2/50 | 2.5 % |
| flammability | Test Condition | Test Method | TRINSEO HK/3453 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| burning rate | 2.00mm | ISO 3795 | 55 mm/min |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| atomization | ISO 294-4 | 97 % | |
| carbon emission | VDA277 | 25.0 µg/g |
| physical property | Test Condition | Test Method | TRINSEO HK/3453 |
|---|---|---|---|
| Shrinkage rate | MD | ISO 294-4 | 0.40-0.70 % |
| Apparent density | ISO 60 | 0.65 g/cm³ | |
| melt mass-flow rate | 230°C/3.8kg | ISO 1133 | 5.0 g/10min |
| 220°C/10.0kg | ISO 1133 | 15 g/10min |
| Thermal performance | Test Condition | Test Method | TRINSEO HK/3453 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 100 °C |
| vicat | ISO 306/B50 | 97.0 °C |