PC/PBT 420SE0-1001 PC/PBT vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Reference Price

PC/PBT SABIC INNOVATIVE NANSHA 420SE0-1001

Injection grade

US$ 4,490 / MT

FOB Guangzhou port, China

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/420SE0-1001
Tensile modulus	5 mm/min	ASTM D 638	11500 Mpa
Bending modulus	1.3 mm/min, 50 mm span	ASTM D 790	9400 Mpa
Rockwell hardness	R	ASTM D 785	119 -
Tensile stress	抗张程度，Break，类型L, 5 mm/min，Yield	ASTM D 638	95 Mpa
bending strength	Break,1.3 mm/min, 50 mm span	ASTM D 790	186 Mpa
Tensile stress	抗张程度，Yield，类型L，5 mm/min	ASTM D 638	95 Mpa
Tensile modulus	拉伸模量,5 mm/min	ASTM D 638	11500 Mpa
Tensile strength	Break，类型L, 5 mm/min	ASTM D 638	95 Mpa
elongation	Break，类型L, 5 mm/min	ASTM D 638	1.2 %
Rockwell hardness	洛氏硬度 R	ASTM D 785	119 -
Bending modulus	挠曲模量，1.3 mm/min, 50 mm span	ASTM D 790	9400 Mpa
Flexural Stress, brk	弯曲强度，Break,1.3 mm/min, 50 mm span	ASTM D 790	186 Mpa
Tensile stress	拉伸伸长,Break，类型L, 5 mm/min，Yield	ASTM D 638	1.2 %
Tensile stress		拉伸伸长,Yield,类型L, 5 mm/min	ASTM D 638	1.2 %
elongation	Yield,类型L, 5 mm/min	ASTM D 638	1.2 %
Tensile strength	Yield，类型L，5 mm/min	ASTM D 638	95 Mpa
thermal performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/420SE0-1001
Hot deformation temperature	1.82 MPa, 6.4 mm, Unannealed	ASTM D 648	204 °C
Hot deformation temperature		1.82 MPa, 6.4 mm, unannealed （Unannealed）	ASTM D 648	204 °C
Linear coefficient of thermal expansion	60℃ to 138℃, flow （Flow）	ASTM E 831	0.0000252 1/℃
Hot deformation temperature	1.82 MPa, 3.2mm, Unannealed	ASTM D 648	200 °C
Hot deformation temperature		0.45 MPa, 6.4 mm， unannealed （Unannealed）	ASTM D 648	215 °C
Relative Temp Index, Meeh w/o impact	相对热指数，非机械冲击性能	UL 746B	140 °C
Hot deformation temperature	0.45 MPa, 6.4 mm，Unannealed	ASTM D 648	215 °C
Hot deformation temperature		0.45 MPa, 3.2 mm, unannealed （未 Annealed）	ASTM D 648	212 °C
Vicat softening temperature	维卡软化温度，等级 B/50	ASTM D 1525	200 °C
Relative Temp Index, Meeh w/impact	相对热指数，机械冲击性能	UL 746B	130 °C
Hot deformation temperature	1.82 MPa, 3.2mm, unannealed （Unannealed）	ASTM D 648	200 °C
Linear coefficient of thermal expansion	-40℃-4O℃, Flow	ASTM E 831	0.0000252 1/℃
Relative Temp Index. Elec	相对热指数，电性能	UL 746B	130 °C
Linear coefficient of thermal expansion	60℃-138℃, Flow	ASTM E 831	0.0000252 1/℃
Hot deformation temperature	0.45 MPa, 3.2 mm, Unannealed	ASTM D 648	212 °C
Linear coefficient of thermal expansion	-40℃ to 4O℃,flow （Flow）	ASTM E 831	0.0000252 1/℃
Physical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/420SE0-1001
Shrinkage rate	Flow, 1.5-3.2 mm	SABIC method	0.3 - 0.5 %
Bi Rong		ASTM D 792	0.62 cm³/g
Shrinkage rate	flow （Flow），3.2 mm	SABIC method	0.5 - 0.7 %
		xflow （Across Flow），3.2-4.6mm	SABIC method	0.6-1 %
		flow （Flow）,1.5-3.2 mm	SABIC method	0.3 - 0.5 %
density		ASTM D 792	1.61 —
Shrinkage rate	flow （Flow），3.2-4.6 mm	SABIC method	0.5 - 0.8 %
		xflow （Across Flow）,1.5-3.2 mm	SABIC method	0.4 - 0.6 %
		Flow，3.2-4.6 mm	SABIC method	0.5 - 0.8 %
		Flow，3.2 mm	SABIC method	0.5 - 0.7 %
Water absorption rate	24 hours	ASTM D 570	0.06 %
Shrinkage rate	Across Flow，3.2-4.6mm	SABIC method	0.6-1 %
density	比重	ASTM D 792	1.61 —
Specific Volume		ASTM D 792	0.62 cm³/g
Shrinkage rate	Across Flow ,1.5-3.2 mm	SABIC method	0.4 - 0.6 %
Physical property type	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/420SE0-1001
Test project	测试条件	测试方法	测试结果测试单位

Supplier Join