Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC URZ2501 IDEMITSU JAPAN
TARFLON™
Casters,Automotive sector,Electronic field,Electrical field
Flame retardant,enhance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | IDEMITSU JAPAN/URZ2501 |
|---|---|---|---|
| Melt volume flow rate | ISO 1133 | 18 cm3/10min | |
| transmittance | 1mmt | 0.1 | |
| Light reflectance | D65 type,10 | 97.5 |
| Supplementary Information | Test Condition | Test Method | IDEMITSU JAPAN/URZ2501 |
|---|---|---|---|
| ISO Shortcut | >PC-MD20-FR(40)< |
| Mechanical properties | Test Condition | Test Method | IDEMITSU JAPAN/URZ2501 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 50 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 90 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 2.7(GPa) kg/cm²(MPa)[Lb/in²] | |
| elongation at break | ASTM D638/ISO 527 | tB 60 % | |
| tensile strength | ASTM D638/ISO 527 | 60 kg/cm²(MPa)[Lb/in²] | |
| Tensile stress | ISO 527-1 | 60 Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | 70 % | |
| bending strength | ISO 178 | 90 Mpa | |
| Flexural modulus | ISO 178 | 2700 Mpa | |
| tensile strength | 屈服 | ISO 527-2 | 50.0 Mpa |
| Tensile modulus | ISO 527-1 | 2500 Mpa | |
| elongation | 断裂 | ISO 527-1 | 60 % |
| Impact strength of cantilever beam gap | ISO 176 | 40 k/Jm2 |
| optical performance | Test Condition | Test Method | IDEMITSU JAPAN/URZ2501 |
|---|---|---|---|
| refractive index | D65 type,10 | 97.5 ISO 13468 | |
| transmittance | 1000µm | ISO 13468-1 | 0.1 % |
| Yellowness Index | 9.0 YI |
| flammability | Test Condition | Test Method | IDEMITSU JAPAN/URZ2501 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | IDEMITSU JAPAN/URZ2501 |
|---|---|---|---|
| Shrinkage rate | TD:2.00mm | 内部方法 | 0.50-0.70 % |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 16 cm3/10min(300℃/1.2kg ) g/10min | |
| density | ASTM D792/ISO 1183 | 1.38 | |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 18.0 cm3/10min |
| Shrinkage rate | MD:2.00mm | 内部方法 | 0.50-0.70 % |
| Thermal performance | Test Condition | Test Method | IDEMITSU JAPAN/URZ2501 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | V-0/1.5mm | |
| Heat distortion temperature | 0.46MPa，HDT | ISO 75-1-2 | 127 °C |
| HDT | ASTM D648/ISO 75 | 120 ℃（℉） | |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 127 °C | |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 117 °C | |
| 1.8MPa，HDT | ISO 75-1-2 | 117 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 6.5E-05 cm/cm/°C |
| RTI Imp | UL 746 | 80.0 °C | |
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| RTI Str | UL 746 | 80.0 °C | |
| RTI Elec | UL 746 | 80.0 °C |