PPS 1140A6 HD9100 JAPAN POLYPLASTIC
DURAFIDE®
small home appliances、Fitness equipment、Electrical field、Electronic field、Automotive sector、sporting goods
Glass fiber reinforced、High rigidity、high strength、High impact resistance、Flame retardant
UL
SGS
REACH
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | JAPAN POLYPLASTIC/1140A6 HD9100 |
|---|---|---|---|
| melt viscosity | 310℃、1000sec | ISO 11443 | 260 Pa.s |
| Water absorption rate | ISO 62 | 0.01 % |
| Supplementary Information | Test Condition | Test Method | JAPAN POLYPLASTIC/1140A6 HD9100 |
|---|---|---|---|
| ColorNumber | HD9100.HD9001 |
| Basic performance | Test Condition | Test Method | JAPAN POLYPLASTIC/1140A6 HD9100 |
|---|---|---|---|
| density | ISO 1183 | 1.66 g/cm |
| Mechanical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/1140A6 HD9100 |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/leA | 10 KJ/m | |
| bending strength | ISO 178 | 260 Mpa | |
| Flexural modulus | ISO 178 | 13200 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 1.7 % |
| tensile strength | ISO 527-1 | 210 Mpa | |
| fracture strain | ISO 527-1 | 1.9 % | |
| tensile strength | ISO 527-2 | 185 Mpa |
| Electrical performance | Test Condition | Test Method | JAPAN POLYPLASTIC/1140A6 HD9100 |
|---|---|---|---|
| Dissipation Factor | 1kHz | IEC 60250 | 1E-03 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 4 | |
| relative permittivity | 1kHz | IEC 60250 | 4.50 |
| Volume resistivity | IEC 60093 | 5E+15 ohms·cm | |
| dielectric strength | 3.00mm | IEC 60243-1 | 16 KV/mm |
| relative permittivity | 1MHz | IEC 60250 | 4.50 |
| Dissipation Factor | 1MHz | IEC 60250 | 2E-03 |
| flammability | Test Condition | Test Method | JAPAN POLYPLASTIC/1140A6 HD9100 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 |
| physical property | Test Condition | Test Method | JAPAN POLYPLASTIC/1140A6 HD9100 |
|---|---|---|---|
| Water absorption rate | 23°C,24hr | ISO 62 | 0.040 % |
| melt viscosity | 310°C,1000sec^-1 | ISO 11443 | 260000 mPa·s |
| Thermal performance | Test Condition | Test Method | JAPAN POLYPLASTIC/1140A6 HD9100 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD | 内部方法 | 4E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa，HDT | ISO 75-1 | 270 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 265 °C | |
| Linear coefficient of thermal expansion | MD | 内部方法 | 1E-05 cm/cm/°C |
| UL flame retardant rating | UL 94 | V-0 |