Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA12 Latigray 82-03 CW/96 F3 LATI S.p.A.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LATI S.p.A./Latigray 82-03 CW/96 F3 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 7.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 10 kJ/m² |
| Electrical performance | Test Condition | Test Method | LATI S.p.A./Latigray 82-03 CW/96 F3 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1E+03 ohms·cm | |
| Surface Resistivity | ASTM D257 | 1E+02 ohms | |
| Electromagnetic reflectivity | Bekiscan-CP | 95 % |
| Mechanical properties | Test Condition | Test Method | LATI S.p.A./Latigray 82-03 CW/96 F3 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 0.80 % |
| tensile strength | 断裂,23°C | ISO 527-2/5 | 40.0 MPa |
| Tensile modulus | 23°C | ISO 527-2/1 | 8900 MPa |
| physical property | Test Condition | Test Method | LATI S.p.A./Latigray 82-03 CW/96 F3 |
|---|---|---|---|
| Shrinkage rate | MD:2.00mm | ISO 294-4 | 0.50to0.90 % |
| density | ISO 1183 | 10.9 g/cm³ | |
| Shrinkage rate | TD:2.00mm | ISO 294-4 | 0.50to0.90 % |
| Thermal performance | Test Condition | Test Method | LATI S.p.A./Latigray 82-03 CW/96 F3 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 160 °C |
| vicat | ISO 306/B50 | 165 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 105 °C |