Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO GFN30F-701S SABIC INNOVATIVE SHANGHAI
NORYL™
Faucet、Shower、Water meter component、Water pump impeller、Water treatment equipment、Water filter
Dimensional stability、Low warpage、Low Specific Gravity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/GFN30F-701S |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 36 kJ/m² |
| 23°C | ISO 180/1U | 32 kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 12 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 39 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 12 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 47 kJ/m² |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/GFN30F-701S |
|---|---|---|---|
| Rockwell hardness | L计秤 | ASTM D785 | 108 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/GFN30F-701S |
|---|---|---|---|
| bending strength | 屈服,50.0mm跨距4 | ASTM D790 | 180 Mpa |
| Tensile modulus | ISO 527-2/1 | 8740 Mpa | |
| ASTM D638 | 9150 Mpa | ||
| elongation | 断裂 | ASTM D638 | 2.0 % |
| bending strength | ISO 178 | 183 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 1.8 % |
| Flexural modulus | ISO 178 | 8710 Mpa | |
| 100mmSpan5 | ASTM D790 | 7170 Mpa | |
| 50.0mm跨距4 | ASTM D790 | 8000 Mpa | |
| tensile strength | 断裂 | ASTM D638 | 116 Mpa |
| 断裂 | ISO 527-2 | 117 Mpa | |
| bending strength | Yield,100mmSpan5 | ASTM D790 | 162 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/GFN30F-701S |
|---|---|---|---|
| Dissipation Factor | 50Hz | ASTM D150 | 9E-04 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 3 |
| Dissipation Factor | 60Hz | ASTM D150 | 9E-04 |
| dielectric constant | 60Hz | ASTM D150 | 2.93 |
| 50Hz | ASTM D150 | 2.93 | |
| dielectric strength | 3.20mm,inOil | ASTM D149 | 22 KV/mm |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 4 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 4 |
| arc resistance | ASTM D495 | PLC7 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 4 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/GFN30F-701S |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Limiting Oxygen Index | ASTM D2863 | 26 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/GFN30F-701S |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.10-0.40 % |
| Melt volume flow rate | 300°C/5.0kg | ISO 1133 | 7.82 cm3/10min |
| Water absorption rate | 24hr | ASTM D570 | 0.060 % |
| melt mass-flow rate | 300°C/5.0kg | ASTM D1238 | 8.7 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/GFN30F-701S |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 138 °C |
| 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 142 °C | |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 3.1E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 158 °C |
| RTI Str | UL 746 | 90.0 °C | |
| Heat distortion temperature | 0.45MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Bf | 143 °C |
| vicat | -- | ISO 306/B120 | 147 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 6.2E-05 cm/cm/°C |
| vicat | -- | ISO 306/B50 | 143 °C |
| RTI Imp | UL 746 | 90.0 °C | |
| Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 137 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 137 °C | |
| RTI Elec | UL 746 | 90.0 °C |