PC CLS1000 MITSUBISHI THAILAND
IUPILON™
glasses、lens
high viscosity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | MITSUBISHI THAILAND/CLS1000 |
|---|---|---|---|
| bending strength | 23°C | ISO 178 | 93.0 Mpa |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 88 kJ/m² |
| Flexural modulus | 23°C | ISO 178 | 2300 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 2400 Mpa |
| elongation at break | 23°C | ISO 527-2 | 5.4 % |
| tensile strength | 23°C | ISO 527-2 | 60.0 Mpa |
| Electrical performance | Test Condition | Test Method | MITSUBISHI THAILAND/CLS1000 |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 31 KV/mm | |
| dielectric constant | 23°C | IEC 60250 | 3.10 1MHz |
| Surface Resistivity | IEC 60093 | 6E+15 Ω.cm | |
| Dissipation Factor | 23°C | IEC 60250 | 9E-03 1MHz |
| Volume resistivity | IEC 60093 | 3E+16 Ω.cm |
| physical property | Test Condition | Test Method | MITSUBISHI THAILAND/CLS1000 |
|---|---|---|---|
| Water absorption rate | (23°C,24hr) | ISO 62 | 0.24 % |
| melt mass-flow rate | 300℃/1.2Kg | ISO 1133 | 5.3 cm3/10min |
| Thermal performance | Test Condition | Test Method | MITSUBISHI THAILAND/CLS1000 |
|---|---|---|---|
| Heat distortion temperature | 1.80MPa退火，HDT | ISO 75-2/Af | 131 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 6.5E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa未退火，HDT | ISO 75-2/Bf | 145 °C |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 6.6E-05 cm/cm/°C |