Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS K-300 DENKA JAPAN
MALECCA
--
heat-resisting
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DENKA JAPAN/K-300 |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | 16 kJ/m² | |
| Impact strength of cantilever beam gap | ASTM D256 | 180 J/m |
| hardness | Test Condition | Test Method | DENKA JAPAN/K-300 |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 116 |
| R级 | ASTM D785 | 114 |
| Mechanical properties | Test Condition | Test Method | DENKA JAPAN/K-300 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2450 Mpa | |
| ASTM D638 | 41.0 Mpa | ||
| tensile strength | 屈服 | ISO 527-2/50 | 48.0 Mpa |
| bending strength | ISO 178 | 79.0 Mpa | |
| Flexural modulus | ISO 178 | 2450 Mpa | |
| bending strength | ASTM D790 | 75.0 Mpa | |
| Nominal tensile fracture strain | ISO 527-2/50 | 21 % | |
| Flexural modulus | ASTM D790 | 2250 Mpa | |
| tensile strength | 断裂 | ISO 527-2/50 | 40.0 Mpa |
| flammability | Test Condition | Test Method | DENKA JAPAN/K-300 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | DENKA JAPAN/K-300 |
|---|---|---|---|
| Shrinkage rate | 2.00mm | 内部方法 | 0.50-0.80 % |
| density | 23°C | ISO 1183 | 1.08 g/cm³ |
| ASTM D792 | 1.06 g/cm³ | ||
| melt mass-flow rate | 220°C/10.0kg | ISO 1133 | 4.0 g/10min |
| Thermal performance | Test Condition | Test Method | DENKA JAPAN/K-300 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/Af | 100 °C |
| 1.8MPa,Unannealed，HDT | ASTM D648 | 110 °C | |
| vicat | ISO 306/B | 120 °C | |
| ASTM D15256 | 120 °C |