POM 7520 ASAHIKASEI ZHANGJIAGANG
TENAC™-C
Industrial applications、Automotive Applications、Engine parts、Shell、Engineering accessories、currency、Fasteners
High mobility、Medium viscosity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ASAHIKASEI ZHANGJIAGANG/7520 |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | 5.0 kJ/m² | |
| Impact strength of cantilever beam gap | ASTM D256 | 61 J/m |
| hardness | Test Condition | Test Method | ASAHIKASEI ZHANGJIAGANG/7520 |
|---|---|---|---|
| Rockwell hardness | M级 | ASTM D785 | 80 |
| R级 | ASTM D785 | 115 |
| Mechanical properties | Test Condition | Test Method | ASAHIKASEI ZHANGJIAGANG/7520 |
|---|---|---|---|
| Taber abraser | ASTM D1044 | 14.0 mg | |
| Tensile modulus | ISO 527-2 | 2800 Mpa | |
| elongation | 断裂 | ASTM D638 | 32 % |
| tensile strength | -- | ASTM D638 | 64.0 Mpa |
| Flexural modulus | ASTMD790 | 2600 Mpa | |
| bending strength | ASTM D790 | 93.0 Mpa | |
| tensile strength | 屈服 | ISO 527-2 | 64.0 Mpa |
| elongation | 断裂 | ISO 527-2 | 30 % |
| Electrical performance | Test Condition | Test Method | ASAHIKASEI ZHANGJIAGANG/7520 |
|---|---|---|---|
| dielectric constant | 23°C,1MHz | ASTM D150 | 3.90 |
| Surface Resistivity | ASTM D257 | 1.0E+16-1.0E+17 ohms | |
| Volume resistivity | 23°C | ASTM D257 | 1.0E+15-1.0E+16 ohms·cm |
| Dissipation Factor | 23°C,1MHz | ASTM D150 | 8E-03 |
| dielectric strength | ASTM D149 | 19 KV/mm | |
| arc resistance | ASTM D495 | 250 sec |
| flammability | Test Condition | Test Method | ASAHIKASEI ZHANGJIAGANG/7520 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | ASAHIKASEI ZHANGJIAGANG/7520 |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 1.6-2.0 % |
| density | ASTMD792 | 1.41 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 30 g/10min |
| Water absorption rate | 23°C,24hr,50%RH | ASTM D570 | 0.20 % |
| Thermal performance | Test Condition | Test Method | ASAHIKASEI ZHANGJIAGANG/7520 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 110 °C |
| 0.45MPa,未退火，HDT | ASTM D648 | 158 °C | |
| thermal conductivity | 0.23 W/m/K | ||
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 157 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 100 °C | |
| specific heat | 1470 J/kg/°C | ||
| Linear coefficient of thermal expansion | MD | ASTMD696 | 1E-04 cm/cm/°C |