Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/PBT HX6600HP 8H4D023 SABIC INNOVATIVE US
XENOY™
Automotive Applications
High mobility、High impact resistance、Dimensional stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/HX6600HP 8H4D023 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 70 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 100 J |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 100 J | |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 20 kJ/m² |
| 23°C | ISO 180/1A | 65 kJ/m² | |
| Suspended wall beam without notch impact strength | -40°C | ISO 180/1U | NoBreak |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/HX6600HP 8H4D023 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 1900 Mpa | |
| elongation | 屈服 | ASTM D638 | 4.0 % |
| tensile strength | 断裂 | ASTM D638 | 35.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2/50 | 4.0 % |
| tensile strength | 断裂 | ISO 527-2/50 | 37.0 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 1900 Mpa |
| Tensile modulus | ASTM D638 | 1900 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 44.0 Mpa |
| elongation | 断裂 | ASTM D638 | 150 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 43.0 Mpa |
| ISO 178 | 64.0 Mpa | ||
| Flexural modulus | ISO 178 | 1800 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 43.0 Mpa |
| Tensile strain | 断裂 | ISO 527-2/50 | 100 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/HX6600HP 8H4D023 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 1.2-1.6 % |
| Melt volume flow rate | 250°C/5.0kg | ISO 1133 | 10.0 cm3/10min |
| MeltViscosity | 260°C,1500sec^-1 | ISO 11443 | 210 Pa·s |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.050 % |
| 饱和,23°C | ISO 62 | 0.40 % | |
| melt mass-flow rate | 250°C/5.0kg | ASTM D1238 | 11 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/HX6600HP 8H4D023 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Bf | 95.0 °C |
| vicat | -- | ISO 306/B120 | 120 °C |
| Linear coefficient of thermal expansion | MD：23to60°C | ISO 11359-2 | 1.3E-04 cm/cm/°C |
| TD：-40到40°C | ASTME831 | 1E-04 cm/cm/°C | |
| TD：-40到40°C | ISO 11359-2 | 1E-04 cm/cm/°C | |
| MD：-40to40°C | ISO 11359-2 | 1E-04 cm/cm/°C | |
| vicat | -- | ISO 306/B50 | 117 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 1E-04 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 60.0 °C |
| vicat | ASTM D152510 | 117 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 60.0 °C |