POM 5013A ASAHI JAPAN
TENAC™
Industrial applications,Automotive Applications
High mobility,Medium viscosity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Mechanical propertiesTest ConditionTest MethodASAHI JAPAN/5013A
bending strengthASTM D790/ISO 178101 kg/cm²(MPa)[Lb/in²]
Impact strength of cantilever beam gapASTM D256/ISO 17969 kg·cm/cm(J/M)ft·lb/in
Flexural modulusASTM D790/ISO 1783040 kg/cm²(MPa)[Lb/in²]
Rockwell hardness-ASTM D78594 M
bending strengthASTM D790101 Mpa
wear resistanceASTM D104413
elongationASTM D638/ISO 52745 %
Rockwell hardness-ASTM D785120 R
elongation at breakASTM D638/ISO 52745 %
Impact strength of cantilever beam gapASTM D25669 J/m
Rockwell hardnessASTM D78594
elongation at breakASTM D63845 %
Flexural modulusASTM D7903040 Mpa
tensile strength ASTM D638/ISO 52768 kg/cm²(MPa)[Lb/in²]
ASTM D63868 Mpa
otherTest ConditionTest MethodASAHI JAPAN/5013A
characteristic汽车部件
Physical propertiesTest ConditionTest MethodASAHI JAPAN/5013A
Shrinkage rateASTM D9551.8-2.2 %
densityASTM D792/ISO 11831.42
melt mass-flow rateASTM D1238/ISO 113322 g/10min
Water absorption rateASTM D570/ISO 620.2 %
physical property Test ConditionTest MethodASAHI JAPAN/5013A
Shrinkage rate垂直方向旭化成法1.8-2.2 %
平行方向旭化成法1.8-2.2 %
Water absorption rateASTM D5700.2 %
Thermal performanceTest ConditionTest MethodASAHI JAPAN/5013A
melt mass-flow rateASTM D123822 g/10min
Heat distortion temperature0.45MPa，HDTASTM D648172 °C
HDTASTM D648/ISO 75172 ℃（℉）
1.82MPa，HDTASTM D648136 °C
Linear coefficient of thermal expansionASTM D696/ISO 1135910 mm/mm.℃
TMA法10