LDPE Osterlene® LD02520 OSTERMAN USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | OSTERMAN USA/Osterlene® LD02520 |
|---|---|---|---|
| Shore hardness | 邵氏D | ASTM D2240 | 50 |
| film | Test Condition | Test Method | OSTERMAN USA/Osterlene® LD02520 |
|---|---|---|---|
| tensile strength | TD:断裂 | ASTM D882 | 19.3 MPa |
| Elmendorf tear strength | MD | ASTM D1922 | 220 g |
| Secant modulus | 1%正割,MD | ASTME111 | 165 MPa |
| Dart impact | ASTM D1709 | 220 g | |
| elongation | MD:断裂 | ASTM D882 | 300 % |
| Elmendorf tear strength | TD | ASTM D1922 | 200 g |
| Secant modulus | 1%正割,TD | ASTME111 | 186 MPa |
| tensile strength | MD:断裂 | ASTM D882 | 20.7 MPa |
| elongation | TD:断裂 | ASTM D882 | 500 % |
| Mechanical properties | Test Condition | Test Method | OSTERMAN USA/Osterlene® LD02520 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | >600 % |
| tensile strength | 断裂 | ASTM D638 | 14.5 MPa |
| Flexural modulus | ASTM D790 | 234 MPa |
| physical property | Test Condition | Test Method | OSTERMAN USA/Osterlene® LD02520 |
|---|---|---|---|
| density | ASTM D1505 | 0.918 g/cm³ | |
| Environmental stress cracking resistance | 100%Igepal | ASTM D1693 | 0.00 hr |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 0.25 g/10min |
| Thermal performance | Test Condition | Test Method | OSTERMAN USA/Osterlene® LD02520 |
|---|---|---|---|
| vicat | ASTM D1525 | 90.0 °C | |
| brittle temperature | ASTM D746 | <-76.0 °C |