Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
EVOH F101B NIPPON GOHSEI
--
--
copolymer、Lubricity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | NIPPON GOHSEI/F101B |
|---|---|---|---|
| Suspended wall beam without notch impact strength | ISO 180 | 2.9 kJ/m² |
| hardness | Test Condition | Test Method | NIPPON GOHSEI/F101B |
|---|---|---|---|
| Rockwell hardness | M计秤 | ISO 2039-2 | 100 |
| film | Test Condition | Test Method | NIPPON GOHSEI/F101B |
|---|---|---|---|
| OTr | 20°C,85%RH | ISO 14663-2 | 0.030 cm³·mm/m²/atm/24hr |
| 20°C,35%RH | ISO 14663-2 | 6E-03 cm³·mm/m²/atm/24hr | |
| 20°C,100%RH | ISO 14663-2 | 0.38 cm³·mm/m²/atm/24hr | |
| Water Vapor Transmission Rate | ASTME96 | 1.6 g·mm/m²/atm/24hr | |
| OTr | 20°C,0%RH | ISO 14663-2 | 4E-03 cm³·mm/m²/atm/24hr |
| 20°C,65%RH | ISO 14663-2 | 8E-03 cm³·mm/m²/atm/24hr | |
| 20°C,90%RH | ISO 14663-2 | 0.060 cm³·mm/m²/atm/24hr |
| Mechanical properties | Test Condition | Test Method | NIPPON GOHSEI/F101B |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2700 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 15 % |
| Flexural modulus | ISO 178 | 3800 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 34.0 Mpa |
| physical property | Test Condition | Test Method | NIPPON GOHSEI/F101B |
|---|---|---|---|
| melt mass-flow rate | 210°C/2.16kg | ISO 1133 | 3.8 g/10min |
| Ethylene content | 内部方法 | 32.0 mol% | |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 1.6 g/10min |
| Thermal performance | Test Condition | Test Method | NIPPON GOHSEI/F101B |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 183 °C | |
| Crystallization peak temperature | ISO 11357-3 | 161 °C | |
| vicat | ISO 306 | 173 °C | |
| Glass Transition Temperature | ISO 11357-2 | 69.0 °C |