Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO/PA GTX9400W-1710 SABIC INNOVATIVE US
NORYL GTX™
Electrical applications、Industrial machinery
High mobility、dimensional stability 、High temperature resistan、Hydrolysis resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | SABIC INNOVATIVE US/GTX9400W-1710 |
|---|---|---|---|
| drying temperature | 95-105 °C | ||
| drying time | 3-4 h |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/GTX9400W-1710 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 无缺口，-30℃ | ASTM D4812 | 769 J/m |
| 无缺口，23℃ | ASTM D4812 | 849 J/m | |
| bending strength | ASTM D790 | 101 Mpa | |
| tensile strength | 断裂 | ASTM D638 | 62 Mpa |
| 屈服 | ASTM D638 | 65 Mpa | |
| Impact strength of cantilever beam gap | 缺口，-30℃ | ASTM D256 | 112 J/m |
| Flexural modulus | ASTM D790 | 2360 Mpa | |
| Impact strength of cantilever beam gap | 缺口，23℃ | ASTM D256 | 256 J/m |
| Tensile modulus | 50mm/min | ASTM D638 | 1960 Mpa |
| tensile strength | 50mm/min | ISO 527 | 69 Mpa |
| Flexural modulus | 2mm/min | ISO 178 | 2710 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/GTX9400W-1710 |
|---|---|---|---|
| Shrinkage rate | flow,3.2mm，垂直 | GE Method | 1.2-1.4 % |
| melt mass-flow rate | ASTM D1238 | 97 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/GTX9400W-1710 |
|---|---|---|---|
| vicat | ASTM D1525 | 212 °C | |
| Heat distortion temperature | 0.45MPa,3.2mm，HDT | ASTM D648 | 191 °C |
| 1.84MPa,3.2mm，HDT | ASTM D648 | 84 °C | |
| vicat | ISO 306 | 203 °C | |
| Heat distortion temperature | 1.82MPa,6.4mm，HDT | ASTM D648 | 170 °C |
| melting temperature | 270-295 °C | ||
| Heat distortion temperature | 0.45MPa,6.4mm，HDT | ASTM D648 | 203 °C |