Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 1300G ASAHI JAPAN
Leona™
Electrical field、Electronic field、Engine hood parts、Automotive sector、component
High rigidity、high strength、Fatigue resistance、Anti creep
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ASAHI JAPAN/1300G |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 72 kJ/m² |
| Other performance | Test Condition | Test Method | ASAHI JAPAN/1300G |
|---|---|---|---|
| Limiting Oxygen Index | 干 | ASTM D-2863 | 23 % |
| hardness | Test Condition | Test Method | ASAHI JAPAN/1300G |
|---|---|---|---|
| Rockwell hardness | M计秤 | ASTM D785 | 96 |
| R计秤 | ISO 2039-2 | 120 | |
| M计秤 | ISO 2039-2 | 96 | |
| R计秤 | ASTM D785 | 120 |
| Basic performance | Test Condition | Test Method | ASAHI JAPAN/1300G |
|---|---|---|---|
| Water absorption rate | 湿 | 1.7 % |
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/1300G |
|---|---|---|---|
| Impact strength of cantilever beam gap | 干(湿) | ASTM D-256 | 127(147) J/m |
| flexural coefficient | 干(湿) | ASTM D-790 | 9.3(6.3) GPa |
| bending strength | ASTM D790 | 289 Mpa | |
| tensile strength | 干(湿) | ASTM D-638 | 186(132) Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 10000 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2 | 190 Mpa |
| Flexural modulus | ASTM D790/ISO 178 | 9320(MPa) kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 289(MPa) kg·cm/cm(J/M)ft·lb/in | |
| Rockwell hardness | ASTM D785 | M96 | |
| Flexural modulus | ASTM D790 | 9300 Mpa | |
| tensile strength | ASTM D638 | 186 Mpa | |
| Taber abraser | 1000Cycles | ASTM D1044 | -- mg |
| Rockwell hardness | 干(湿) | ASTM D-785 | 120(112) R scale |
| 干(湿) | ASTM D-785 | 96(75) M Scale | |
| elongation | 断裂 | ASTM D638 | 3.0 % |
| Tensile strain | 断裂,23°C | ISO 527-2 | 3.0 % |
| bending strength | 23°C | ISO 178 | 275 Mpa |
| 干(湿) | ASTM D-790 | 289(216) Mpa | |
| Flexural modulus | 23°C | ISO 178 | 9000 Mpa |
| elongation at break | 干(湿) | ASTM D-638 | 3(5) % |
| Electrical performance | Test Condition | Test Method | ASAHI JAPAN/1300G |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | 3.00mm | IEC 60112 | PLC 0 |
| Volume resistivity | ASTM D257 | 1E+15 ohms·cm | |
| dielectric strength | IEC 60243-1 | 28 KV/mm | |
| Surface Resistivity | ASTM D257 | 1E+15 ohms | |
| dielectric strength | ASTM D149 | 28 KV/mm | |
| Volume resistivity | 23°C | IEC 60093 | 1E+15 ohms·cm |
| arc resistance | ASTM D495/IEC 60112 | 124 | |
| Surface Resistivity | IEC 60093 | 1E+15 ohms |
| other | Test Condition | Test Method | ASAHI JAPAN/1300G |
|---|---|---|---|
| characteristic | 高刚性 |
| Physical properties | Test Condition | Test Method | ASAHI JAPAN/1300G |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.4-0.9 % | |
| density | ASTM D792/ISO 1183 | 1.39 | |
| Water absorption rate | ASTM D570/ISO 62 | 1.7 % |
| flammability | Test Condition | Test Method | ASAHI JAPAN/1300G |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| Limiting Oxygen Index | ASTM D2863 | 23 % |
| physical property | Test Condition | Test Method | ASAHI JAPAN/1300G |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 0.40 % |
| Wear factor | 湿 | ASTM D-1044 | 15 ×10-6kg/1000times |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | -- % |
| Shrinkage rate | 吸水率(饱和,23°C) | 内部方法 | -- % |
| TD | 内部方法 | 0.90 % | |
| 干 | 旭化成方法 | 0.4/0.9 % |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/1300G |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 250 °C |
| Combustibility (rate) | UL 94 | HB | |
| specific heat | 干 | 1590 J/(kg.k) | |
| Linear coefficient of thermal expansion | 干 | ASTM D-696 | 3 ×10-5/K |
| ASTM D696/ISO 11359 | 3 mm/mm.℃ | ||
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 260 °C |
| 1.82MPa,干，HDT | ASTM D-648 | 250 °C | |
| thermal conductivity | 0.30 W/m/K | ||
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 250 ℃（℉） |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 265 °C | |
| 0.46MPa,干，HDT | ASTM D-648 | 260 °C | |
| thermal conductivity | 干 | 0.3 W/(m.K) | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 250 °C |
| UL flame retardant rating | 干 | UL 94 | HB |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 3E-05 cm/cm/°C |
| specific heat | 1590 J/kg/°C |