Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO N1250 BK1066 SABIC INNOVATIVE SHANGHAI
NORYL™
Automotive interior parts、Electrical applications
High temperature resistan、High mobility、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/N1250 BK1066 |
|---|---|---|---|
| Dart impact | 23°C, Total Energy | ASTM D3763 | 40.0 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/N1250 BK1066 |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2680 Mpa | |
| elongation | 断裂 | ASTM D638 | 25 % |
| 屈服 | ASTM D638 | 4.6 % | |
| bending strength | 屈服, 50.0 mm 跨距 | ASTM D790 | 113 Mpa |
| tensile strength | 断裂 | ASTM D638 | 64.0 Mpa |
| 屈服 | ASTM D638 | 75.0 Mpa | |
| Flexural modulus | 50.0 mm 跨距 | ASTM D790 | 2680 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/N1250 BK1066 |
|---|---|---|---|
| Hot wire ignition (HWI) | UL 746 | PLC 0 | |
| arc resistance | ASTM D495 | PLC 6 | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 2 | |
| High arc combustion index (HAI) | UL 746 | PLC 0 | |
| High Voltage Arc Resistance Index (HVAR) (PLC) | UL 746 | PLC 4 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/N1250 BK1066 |
|---|---|---|---|
| UL flame retardant rating | 2.5 mm | UL 94 | 5VA |
| 0.40 mm | UL 94 | V-2 | |
| 0.76 mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/N1250 BK1066 |
|---|---|---|---|
| melt mass-flow rate | 300°C/5.0 kg | ASTM D1238 | 28 g/10 min |
| Shrinkage rate | 3.20 mm，Flow | 内部方法 | 0.50 - 0.70 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/N1250 BK1066 |
|---|---|---|---|
| Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ASTM E831 | 6.1E-5 cm/cm/°C |
| vicat | ASTM D15255 | 137 °C | |
| Heat distortion temperature | 0.45 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 131 °C |
| 1.8 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 122 °C | |
| RTI Imp | UL 746 | 105 °C | |
| Linear coefficient of thermal expansion | 横向 : -40 到 40°C | ASTM E831 | 6.8E-5 cm/cm/°C |
| RTI | UL 746 | 115 °C | |
| Heat distortion temperature | 0.45 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 133 °C |
| 1.8 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 116 °C | |
| RTI Elec | UL 746 | 110 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/N1250 BK1066 |
|---|---|---|---|
| screw speed | 20 to 100 rpm | ||
| Suggested maximum moisture content | 0.020 % | ||
| Processing (melt) temperature | 275 to 305 °C | ||
| drying temperature | 105 to 110 °C | ||
| Suggested injection volume | 30 to 70 % | ||
| drying time | 3.0 to 4.0 hr | ||
| Temperature in the middle of the barrel | 255 to 300 °C | ||
| Temperature at the rear of the barrel | 245 to 295 °C | ||
| Exhaust hole depth | 0.038 to 0.051 mm | ||
| Temperature at the front of the material cylinder | 265 to 305 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| Temperature | 70 to 100 °C | ||
| Spray nozzle temperature | 275 to 305 °C |