Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS TN-7000 TEIJIN JAPAN
MULTILON®
Electrical applications,Computer components,OA device,Business equipment
Flame retardant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TEIJIN JAPAN/TN-7000 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | NoBreak |
| Mechanical properties | Test Condition | Test Method | TEIJIN JAPAN/TN-7000 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2600 Mpa | |
| Tensile stress | 断裂 | ISO 527-1 | 48 Mpa |
| Tensile strain | 屈服 | ISO 527-2/50 | 3.0 % |
| tensile strength | 断裂 | ISO 527-2/50 | 48.0 Mpa |
| Tensile stress | ISO 527-1 | 63 Mpa | |
| Impact strength of cantilever beam gap | 带缺口 | ISO 179 | 15 KJ/m |
| tensile strength | 屈服 | ISO 527-2/50 | 63.0 Mpa |
| bending strength | ISO 178 | 95 Mpa | |
| Flexural modulus | ISO 178 | 2600 Mpa | |
| Impact strength of cantilever beam gap | 没缺口 | ISO 179 | NB KJ/m |
| elongation at break | ISO 527-1 | 80 % | |
| Tensile strain | 断裂 | ISO 527-2/50 | 80 % |
| elongation at yield | ISO 527-1 | 3 % | |
| Tensile modulus | ISO 527-1 | 2600 Mpa |
| Electrical performance | Test Condition | Test Method | TEIJIN JAPAN/TN-7000 |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 1E+16 ohms |
| flammability | Test Condition | Test Method | TEIJIN JAPAN/TN-7000 |
|---|---|---|---|
| UL flame retardant rating | 2.0mm | UL 94 | 5VB |
| 0.70mm | UL 94 | V-2 | |
| 1.2mm | UL 94 | V-1 | |
| 1.5mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | TEIJIN JAPAN/TN-7000 |
|---|---|---|---|
| Shrinkage rate | 平行方向 | 0.5-0.7 % | |
| 垂直方向 | 0.5-0.7 % | ||
| MD:4.00mm | 内部方法 | 0.50-0.70 % | |
| TD:4.00mm | 内部方法 | 0.50-0.70 % |
| Thermal performance | Test Condition | Test Method | TEIJIN JAPAN/TN-7000 |
|---|---|---|---|
| vicat | ISO 306 | 97 °C | |
| Linear coefficient of thermal expansion | 垂直方向 | ISO 11359-2 | 0.8 |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 94.0 °C |
| Linear coefficient of thermal expansion | 平行方向 | ISO 11359-2 | 0.8 |
| vicat | ISO 306/B50 | 97.0 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 84.0 °C |
| 1.80MPa，HDT | ISO 75-1 | 84 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 8E-05 cm/cm/°C |
| Heat distortion temperature | 0.45Mpa，HDT | ISO 75-2 | 94 °C |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 8E-05 cm/cm/°C |
| UL flame retardant rating | UL 94 | V-0 |