ABS PA-763A TAIWAN CHIMEI
POLYLAC® 
Electrical field,Electronic field
Flame retardant,High impact resistance,High temperature resistan
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

hardnessTest ConditionTest MethodTAIWAN CHIMEI/PA-763A
Rockwell hardnessR-ScaleASTM D78598
thermal performanceTest ConditionTest MethodTAIWAN CHIMEI/PA-763A
Hot deformation temperature1.8MPa,UnannealedASTM D64885.0 °C
1.8MPa,UnannealedISO 75-2/A86.0 °C
1.8MPa,AnnealedASTMD64896.0 °C
Linear coefficient of thermal expansionMDISO 11359-28.5E-05 cm/cm/°C
Vicat softening temperature--ISO 306/B5096.0 °C
--ASTM D15257104 °C
--ISO 306/A50103 °C
mechanical propertiesTest ConditionTest MethodTAIWAN CHIMEI/PA-763A
Bending modulus--5ASTM D7902410 Mpa
--6ISO 1782000 Mpa
bending strength--5ASTM D79060.7 Mpa
--6ISO 17858.0 Mpa
elongationBreak4ASTM D63830 %
BreakISO 527-2/5015 %
tensile strengthYieldISO 527-2/5038.0 Mpa
BreakISO 527-2/5029.0 Mpa
Yield4ASTM D63838.6 Mpa
Physical propertiesTest ConditionTest MethodTAIWAN CHIMEI/PA-763A
density23°CISO 11831.19 g/cm³
--3ASTM D7921.19 g/cm³
melt mass-flow rate200°C/5.0kgASTM D12382.8 g/10min
Melt Volume Flow Rate (MVR)220°C/10.0kgISO 113327.0 cm3/10min
Shrinkage rateISO 294-40.30-0.60 %
impact performanceTest ConditionTest MethodTAIWAN CHIMEI/PA-763A
Charpy Notched Impact Strength-30°CISO 17912 kJ/m²
23°CISO 17922 kJ/m²
Impact strength of cantilever beam gap-30°CISO 180/1A11 kJ/m²
23°CISO 180/1A21 kJ/m²
23°C,3.20mmASTM D256230 J/m
23°C,6.40mmASTM D256200 J/m
flammabilityTest ConditionTest MethodTAIWAN CHIMEI/PA-763A
UL flame retardant rating2.5mmUL 945VA
1.5mmUL 94V-0