PP Homopolymer Braskem PP H358-02 Braskem America Inc.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Braskem America Inc./Braskem PP H358-02 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C,注塑 | ISO 179/1eA | 6.5 kJ/m² |
| film | Test Condition | Test Method | Braskem America Inc./Braskem PP H358-02 |
|---|---|---|---|
| Thin film puncture strength | 30µm | ASTM D5748 | 61.0 N |
| Tensile modulus | 1%正割,MD:30µm,铸造薄膜 | ISO 527-3 | 600 MPa |
| film thickness | 30 µm | ||
| Thin film puncture strength | 30µm | ASTM D5748 | 2.80 J |
| Tensile modulus | 1%正割,TD:30µm,铸造薄膜 | ISO 527-3 | 570 MPa |
| Mechanical properties | Test Condition | Test Method | Braskem America Inc./Braskem PP H358-02 |
|---|---|---|---|
| Flexural modulus | 注塑 | ISO 178 | 1350 MPa |
| tensile strength | 屈服,注塑 | ISO 527-2 | 33.0 MPa |
| Tensile strain | 屈服,注塑 | ISO 527-2 | 13 % |
| optical performance | Test Condition | Test Method | Braskem America Inc./Braskem PP H358-02 |
|---|---|---|---|
| Haze ratio | 30.0µm,铸造薄膜 | ASTM D1003 | 1.4 % |
| gloss | 45°,30.0µm,铸造薄膜 | ASTM D2457 | 80 |
| physical property | Test Condition | Test Method | Braskem America Inc./Braskem PP H358-02 |
|---|---|---|---|
| density | ISO 1183 | 0.900 g/cm³ | |
| melt mass-flow rate | 230°C/2.16kg | ISO 1133 | 2.1 g/10min |
| Thermal performance | Test Condition | Test Method | Braskem America Inc./Braskem PP H358-02 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 105 °C |
| vicat | ISO 306/A | 155 °C |