PC DCL-4532 BK SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Automotive components,Electronic and electrical components,Sports equipment
Thermal stability,High temperature resistan,Hydrolysis resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/DCL-4532 BK |
|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,64.0mmSpan | ISO 75-2/Bf | 148 °C |
| 1.8MPa,未退火,64.0mm跨距 | ISO 75-2/Af | 144 °C | |
| 1.8MPa,未退火,3.20mm | ASTM D648 | 144 °C | |
| 0.45MPa,未退火,3.20mm | ASTM D648 | 148 °C | |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 6.3E-05 cm/cm/°C |
| TD：-40到40°C | ISO 11359-2 | 6.3E-05 cm/cm/°C | |
| MD：-40到40°C | ISO 11359-2 | 4.1E-05 cm/cm/°C | |
| MD：-40到40°C | ASTME831 | 4.1E-05 cm/cm/°C |
| mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/DCL-4532 BK |
|---|---|---|---|
| Bending modulus | ASTM D790 | 6210 Mpa | |
| ISO 178 | 6700 Mpa | ||
| bending strength | ISO 178 | 142 Mpa | |
| ASTM D790 | 138 Mpa | ||
| elongation | 断裂 | ASTM D638 | 2.1 % |
| 屈服 | ASTM D638 | 2.1 % | |
| Friction coefficient | Dynamic | ASTM D3702Modified | 0.36 |
| Static | ASTM D3702Modified | 0.37 | |
| Tensile modulus | ASTM D638 | 7580 Mpa | |
| ISO 527-2/1 | 7470 Mpa | ||
| Tensile strain | 屈服 | ISO 527-2 | 2.2 % |
| 断裂 | ISO 527-2 | 2.2 % | |
| tensile strength | 屈服 | ASTM D638 | 91.7 Mpa |
| 屈服 | ISO 527-2 | 93.0 Mpa | |
| 断裂 | ASTM D638 | 91.7 Mpa | |
| 断裂 | ISO 527-2 | 93.0 Mpa | |
| Wear factor | Washer | ASTM D3702Modified | 49.0 10^-10in^5-min/ft-lb-hr |
| Physical properties | Test Condition | Test Method | SABIC INNOVATIVE US/DCL-4532 BK |
|---|---|---|---|
| Shrinkage rate | TD:24小时 | ISO 294-4 | 0.54 % |
| TD：24hr | ASTM D955 | 0.40-0.60 % | |
| MD：24小时 | ASTM D955 | 0.30-0.50 % | |
| MD:24小时 | ISO 294-4 | 0.43 % | |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.10 % |
| impact performance | Test Condition | Test Method | SABIC INNOVATIVE US/DCL-4532 BK |
|---|---|---|---|
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 18.6 J |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 9.1 kJ/m² |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 5.30 J | |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 29 kJ/m² |