Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS 450Y TORAY JAPAN
Toyolac®
Industrial machinery
Easy to spray、Easy electroplating、heat-resisting
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TORAY JAPAN/450Y |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 16 kJ/m² |
| Impact strength of cantilever beam gap | -30°C,12.7mm | ASTM D256 | 91 J/m |
| 23°C,12.7mm | ASTM D256 | 150 J/m | |
| -30°C,3.20mm | ASTM D256 | 98 J/m |
| hardness | Test Condition | Test Method | TORAY JAPAN/450Y |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | ASTM D785 | 111 |
| R计秤,23°C | ISO 2039-2 | 111 |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/450Y |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 12 % |
| Tensile strain | 断裂,23°C | ISO 527-2 | 10 % |
| bending strength | 23°C | ISO 178 | 80.0 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2 | 53.0 Mpa |
| bending strength | ASTM D790 | 77.0 Mpa | |
| Flexural modulus | 23°C | ISO 178 | 2360 Mpa |
| ASTM D790 | 2300 Mpa | ||
| tensile strength | ASTM D638 | 46.0 Mpa |
| flammability | Test Condition | Test Method | TORAY JAPAN/450Y |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | TORAY JAPAN/450Y |
|---|---|---|---|
| density | 23°C | ISO 1183 | 1.07 g/cm³ |
| Shrinkage rate | 内部方法 | 0.50-0.80 % | |
| density | ASTM D792 | 1.07 g/cm³ | |
| melt mass-flow rate | 220°C/10.0kg | ISO 1133 | 6.0 g/10min |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/450Y |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 98.0 °C |
| vicat | 105 °C | ||
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 95.0 °C |