PC GSH2020DT 9010 MITSUBISHI THAILAND
IUPILON™
Automotive Applications,electrical equipment,Camera applications
Glass fiber reinforced,Filler: Glass fiber reinf,20% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | MITSUBISHI THAILAND/GSH2020DT 9010 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 12 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 58 kJ/m² |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI THAILAND/GSH2020DT 9010 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 6200 Mpa | |
| bending strength | ISO 178 | 160 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 2.8 % |
| Flexural modulus | ISO 178 | 6200 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 105 Mpa |
| Electrical performance | Test Condition | Test Method | MITSUBISHI THAILAND/GSH2020DT 9010 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 3 |
| flammability | Test Condition | Test Method | MITSUBISHI THAILAND/GSH2020DT 9010 |
|---|---|---|---|
| UL flame retardant rating | 0.40mm | UL 94 | HB |
| physical property | Test Condition | Test Method | MITSUBISHI THAILAND/GSH2020DT 9010 |
|---|---|---|---|
| Shrinkage rate | TD:3.20mm | 0.30-0.50 % | |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 8.50 cm3/10min |
| Shrinkage rate | 吸水率(饱和,23°C) | 0.14 % | |
| MD:3.20mm | 0.10-0.30 % | ||
| density | ISO 1183 | 1.35 g/cm³ | |
| melt mass-flow rate | 300°C/1.2kg | ISO 1133 | 9.0 g/10min |
| Thermal performance | Test Condition | Test Method | MITSUBISHI THAILAND/GSH2020DT 9010 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 144 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 139 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 2.6E-05 cm/cm/°C |
| TD | ISO 11359-2 | 6.1E-05 cm/cm/°C |