Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS 6465A6 JAPAN POLYPLASTIC
DURAFIDE®
Household appliances、Fiber grade
High temperature resistan、High gloss、Flame retardant、Glass fiber reinforced、enhance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | JAPAN POLYPLASTIC/6465A6 |
|---|---|---|---|
| Rockwell hardness | M级 | ISO 2039-2 | 105 |
| Supplementary Information | Test Condition | Test Method | JAPAN POLYPLASTIC/6465A6 |
|---|---|---|---|
| ColorNumber | HD9050 |
| Basic performance | Test Condition | Test Method | JAPAN POLYPLASTIC/6465A6 |
|---|---|---|---|
| melt viscosity | ISO 11443 | 280 Pa.s | |
| ASTM D3835 | 270 Pa.s |
| Mechanical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/6465A6 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 200 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 19000 kg/cm²(MPa)[Lb/in²] | |
| Tensile stress | 屈服 | ASTM D638 | 145 MPa |
| elongation at break | ASTM D638/ISO 527 | 1 % | |
| Impact strength of cantilever beam gap | ASTM D256 | 75 J/m | |
| tensile strength | ASTM D638/ISO 527 | 140 kg/cm²(MPa)[Lb/in²] | |
| ISO 527-2 | 140 Mpa | ||
| elongation | 断裂 | ASTM D638 | 1.2 % |
| Charpy Notched Impact Strength | ISO 179/1eA | 6.0 kJ/m² | |
| Tensile stress | 屈服 | ISO 527-2 | 140 MPa |
| bending strength | ISO 178 | 200 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 1.0 % |
| Flexural modulus | ISO 178 | 19000 Mpa | |
| elongation | 断裂 | ISO 527-2 | 1.0 % |
| Electrical performance | Test Condition | Test Method | JAPAN POLYPLASTIC/6465A6 |
|---|---|---|---|
| Dissipation Factor | 1kHz | IEC 60250 | 2E-03 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
| relative permittivity | 1kHz | IEC 60250 | 4.80 |
| Dissipation Factor | 耐电弧性 | IEC 60250 | 170 sec |
| Volume resistivity | IEC 60093 | 2E+15 ohms·cm | |
| dielectric strength | 3.00mm | IEC 60243-1 | 15 KV/mm |
| relative permittivity | 1MHz | IEC 60250 | 4.80 |
| Volume resistivity | ASTM D257/IEC 60093 | - Ω.cm | |
| Dissipation Factor | 1MHz | IEC 60250 | 2E-03 |
| Physical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/6465A6 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.95 | |
| Water absorption rate | ASTM D570/ISO 62 | - % |
| flammability | Test Condition | Test Method | JAPAN POLYPLASTIC/6465A6 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 |
| physical property | Test Condition | Test Method | JAPAN POLYPLASTIC/6465A6 |
|---|---|---|---|
| Water absorption rate | 23°C,24hr | ISO 62 | 0.030 % |
| melt viscosity | 310°C,1000sec^-1 | ISO 11443 | 280000 mPa·s |
| Thermal performance | Test Condition | Test Method | JAPAN POLYPLASTIC/6465A6 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | V-0 | |
| Linear coefficient of thermal expansion | TD | 内部方法 | 3E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 275 ℃ |
| 1.8MPa,未退火，HDT | ISO 75-2A | 270 ℃ | |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 270 °C | |
| Linear coefficient of thermal expansion | MD | 内部方法 | 1E-05 cm/cm/°C |
| ASTM D696/ISO 11359 | - mm/mm.℃ | ||
| UL flame retardant rating | UL 94 | V-0 |