UHMWPE X 188 CELANESE USA
GUR®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | CELANESE USA/X 188 |
|---|---|---|---|
| Charpy Double 14°V-Notch Strength | 23°C | ISO 11542-2 | 90.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | CELANESE USA/X 188 |
|---|---|---|---|
| Tensile stress | 50% 应变 | ISO 527-2/1B | 18.0 Mpa |
| Nominal tensile fracture strain | ISO 527-2/1B | 800 % | |
| Tensile strain | 屈服 | ISO 527-2/1B | 8.0 % |
| Tensile stress | 断裂 | ISO 527-2/1B | 38.0 Mpa |
| Wear by Sandslurry Method?5 | 内部方法 | 200 | |
| Tensile modulus | ISO 527-2/1B | 950 Mpa | |
| Tensile stress | 屈服 | ISO 527-2/1B | 24.0 Mpa |
| physical property | Test Condition | Test Method | CELANESE USA/X 188 |
|---|---|---|---|
| Viscosity Number (Reduced Viscosity) | -- | ISO 1628 | 600.0 ml/g |
| Apparent density | ISO 60 | 0.45 g/cm³ | |
| Viscosity Number (Reduced Viscosity) | -- 2 | ISO 1628 | 600.0 ml/g |
| Average molecular weight 3 | 700000 g/mol | ||
| melt mass-flow rate | 190°C/21.6 kg | ISO 1133 | 0.50 g/10 min |
| Viscosity Number (Reduced Viscosity) | Elongational Stress F - 150/10 | ISO 11542-2 | < 0.0500 Mpa |
| Average particle size - d50 4 | 115 |
| Thermal performance | Test Condition | Test Method | CELANESE USA/X 188 |
|---|---|---|---|
| vicat | ISO 306/B50 | 80.0 °C |