Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO WCD891B-BK1066 SABIC INNOVATIVE SHANGHAI
FLEX NORYL™
Automotive interior parts
High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/WCD891B-BK1066 |
|---|---|---|---|
| Shore hardness | 邵氏 A, 30 秒 | ASTM D2240 | 89 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/WCD891B-BK1066 |
|---|---|---|---|
| Tensile strain | 断裂, 113°C5 | UL 1581 | 160 % |
| 断裂2 | UL 1581 | 220 % | |
| Flexural modulus | -- | ISO 178 | 140 Mpa |
| tensile strength | 断裂2 | UL 1581 | 18.0 Mpa |
| 断裂, 113°C4 | UL 1581 | 21.0 Mpa | |
| Tensile strain | 断裂3 | ASTM D638 | 170 % |
| tensile strength | 断裂3 | ASTM D638 | 16.0 Mpa |
| Flexural modulus | 100 mm 跨距 | ASTM D790 | 160 Mpa |
| Tensile strain | 屈服 | ISO 527-2/50 | 140 % |
| tensile strength | 断裂 | ISO 527-2/50 | 15.0 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/WCD891B-BK1066 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| Dissipation Factor | 1 MHz | IEC 60250 | 4.0E-3 |
| Volume resistivity | ASTM D257 | 1.5E+15 ohms·cm | |
| Surface Resistivity | ASTM D257 | 5.1E+15 ohms | |
| relative permittivity | 1 MHz | IEC 60250 | 2.90 |
| dielectric strength | 2.00 mm, 在油中 | IEC 60243-1 | 24 KV/mm |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/WCD891B-BK1066 |
|---|---|---|---|
| Hot filament ignition temperature | 3.0 mm | IEC 60695-2-13 | 750 °C |
| Burning wire flammability index | 3.0 mm | IEC 60695-2-12 | 850 °C |
| Limiting Oxygen Index | VW-12 | UL 1581 | Pass |
| ISO 4589-2 | 27 % | ||
| UL flame retardant rating | 4.0 mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/WCD891B-BK1066 |
|---|---|---|---|
| melt mass-flow rate | 250°C/5.0 kg | ASTM D1238 | 20 g/10 min |
| elastomer | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/WCD891B-BK1066 |
|---|---|---|---|
| tear strength | ISO 6383 | 7.0 kN/m |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/WCD891B-BK1066 |
|---|---|---|---|
| Heat distortion temperature | 100°C | UL 1581 | 9.0 % |
| brittle temperature | ASTM D746 | < -40.0 °C | |
| UL temperature rating | UL 1581 | 80 °C |