EPE ELITE™ AT 6202 DOW USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Supplementary Information | Test Condition | Test Method | DOW USA/ELITE™ AT 6202 |
---|---|---|---|
VFFSHotTackwindow | 内部方法 | 45°F(205-250 |
film | Test Condition | Test Method | DOW USA/ELITE™ AT 6202 |
---|---|---|---|
Thin film puncture strength | 25µm | 内部方法 | 54.3 N |
25µm | 内部方法 | 20.9 J/cm³ | |
tensile strength | TD:屈服,25µm | ASTM D882 | 7.79 MPa |
elongation | TD:断裂,25µm | ASTM D882 | 600 % |
Elmendorf tear strength | TD:25µm | ASTM D1922 | 430 g |
elongation | MD:断裂,25µm | ASTM D882 | 450 % |
Secant modulus | 2%正割,TD:25µm | ASTM D882 | 77.2 MPa |
Thin film puncture strength | 25µm | 内部方法 | 4.29 J |
film thickness | 25 µm | ||
tensile strength | MD:屈服,25µm | ASTM D882 | 7.93 MPa |
TD:断裂,25µm | ASTM D882 | 40.0 MPa | |
Secant modulus | 2%正割,MD:25µm | ASTM D882 | 68.9 MPa |
Dart impact | 25µm | ASTM D1709B | 1000 g |
Elmendorf tear strength | MD:25µm | ASTM D1922 | 210 g |
tensile strength | MD:断裂,25µm | ASTM D882 | 49.0 MPa |
optical performance | Test Condition | Test Method | DOW USA/ELITE™ AT 6202 |
---|---|---|---|
gloss | 45°,25.4µm | ASTM D2457 | 63 |
Haze ratio | 25.4µm | ASTM D1003 | 7.9 % |
physical property | Test Condition | Test Method | DOW USA/ELITE™ AT 6202 |
---|---|---|---|
density | ASTM D792 | 0.908 g/cm³ | |
melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 0.85 g/10min |
Thermal performance | Test Condition | Test Method | DOW USA/ELITE™ AT 6202 |
---|---|---|---|
melting temperature | 内部方法 | 106 °C |