PSU S2010 BASF GERMANY
Ultrason®S
Food containers、Medical equipment
High temperature resistan、wear resistant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF GERMANY/S2010 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 5.5 kJ/m² |
| -30°C | ISO 179 | 6.0 kJ/m² | |
| Impact strength of cantilever beam gap | 23°C | ISO 180 | 5.5 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | NoBreak |
| Impact strength of cantilever beam gap | -30°C | ISO 180 | 6.0 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179 | NoBreak |
| hardness | Test Condition | Test Method | BASF GERMANY/S2010 |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 135 Mpa |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/S2010 |
|---|---|---|---|
| tensile strength | 屈服,23°C | ISO 527-2 | 75.0 Mpa |
| Tensile strain | 屈服,23°C | ISO 527-2 | 6.0 % |
| Tensile modulus | 23°C | ISO 527-2 | 2550 Mpa |
| Electrical performance | Test Condition | Test Method | BASF GERMANY/S2010 |
|---|---|---|---|
| dielectric constant | 100Hz | IEC 60250 | 3.10 |
| dielectric strength | IEC 60243-1 | 40 KV/mm | |
| Volume resistivity | IEC 60093 | >1.0E+13 ohms·cm | |
| Dissipation Factor | 100Hz | IEC 60250 | 8E-04 |
| dielectric constant | 1MHz | IEC 60250 | 3.10 |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 6.4E-03 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| flammability | Test Condition | Test Method | BASF GERMANY/S2010 |
|---|---|---|---|
| UL flame retardant rating | 3.2mm | UL 94 | V-2 |
| 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | BASF GERMANY/S2010 |
|---|---|---|---|
| Melt volume flow rate | 360°C/10.0kg | ISO 1133 | 90.0 cm3/10min |
| Shrinkage rate | TD | ISO 294-4 | 0.72 % |
| MD | ISO 294-4 | 0.68 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.30 % |
| 饱和,23°C | ISO 62 | 0.80 % | |
| density | ISO 1183 | 1.23 g/cm³ |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/S2010 |
|---|---|---|---|
| RTI Imp | 3.2mm | UL 746 | 130 °C |
| Linear coefficient of thermal expansion | MD | 5.3E-05 cm/cm/°C | |
| RTI Imp | 1.6mm | UL 746 | 130 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 176 °C |
| RTI Elec | 3.2mm | UL 746 | 155 °C |
| RTI Str | 1.6mm | UL 746 | 155 °C |
| RTI Elec | 1.6mm | UL 746 | 155 °C |
| RTI Str | 3.2mm | UL 746 | 155 °C |