PPA UX08325 BK8115 SABIC INNOVATIVE NANSHA
LNP™ THERMOCOMP™
Mechanical parts、consumer goods
Thermal stability、Carbon fiber reinforced、Filler: Glass fiber reinf
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/UX08325 BK8115 |
|---|---|---|---|
| 23°C | ISO 180/1A | 2.9 kJ/m² | |
| ASTM D256 | 31 J/m | ||
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 350 J/m |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/UX08325 BK8115 |
|---|---|---|---|
| dielectric constant | 1.00GHz | ASTM D150 | 4.20 |
| Dissipation Factor | 1.00GHz | ASTM D150 | 0.010 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/UX08325 BK8115 |
|---|---|---|---|
| fracture | ISO 527-2/5 | 125 Mpa | |
| ASTM D638 | 1.9 % | ||
| --6 | ISO 178 | 194 Mpa | |
| Yield, 50.0mm span | ASTM D790 | 197 Mpa | |
| --5 | ISO 178 | 9610 Mpa | |
| fracture | ASTM D638 | 135 Mpa | |
| 50.0mm span | ASTM D790 | 9770 Mpa | |
| Fracture bending strain | ISO 178 | 2.1 % | |
| --1 | ASTM D638 | 10900 Mpa | |
| fracture | ISO 527-2/5 | 1.6 % | |
| Fracture, 50.0mm span | ASTM D790 | 195 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/UX08325 BK8115 |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 0.42 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.54 % |
| Shrinkage rate | TD | 内部方法 | 0.53 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/UX08325 BK8115 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD:-40到40°C | ASTME831 | 5.4E-05 cm/cm/°C |
| 1.8MPa, Unanealed, 64.0mm span | ISO 75-2/Af | 262 °C | |
| 1.8MPa, Unanealed, 3.20mm | ASTM D648 | 264 °C | |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 2.2E-05 cm/cm/°C |