POM 4013A ASAHI JAPAN
TENAC™
Automotive interior parts
Weather resistance、UV resistance、Medium viscosity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Mechanical propertiesTest ConditionTest MethodASAHI JAPAN/4013A
bending strengthASTM D790/ISO 17898 kg/cm²(MPa)[Lb/in²]
Impact strength of cantilever beam gapASTM D256/ISO 17978 kg·cm/cm(J/M)ft·lb/in
Flexural modulusASTM D790/ISO 1783040 kg/cm²(MPa)[Lb/in²]
Rockwell hardness-ASTM D78594 M
bending strengthASTM D79098 Mpa
wear resistanceASTM D104413
Rockwell hardness-ASTM D785120 R
elongation at breakASTM D638/ISO 52755 %
Impact strength of cantilever beam gapASTM D25678 J/m
Rockwell hardnessASTM D78594
elongation at breakASTM D63855 %
Flexural modulusASTM D7903040 Mpa
tensile strength ASTM D638/ISO 52767 kg/cm²(MPa)[Lb/in²]
ASTM D63867 Mpa
otherTest ConditionTest MethodASAHI JAPAN/4013A
characteristic含UV紫外线吸收剂和其他耐气候助剂
Physical propertiesTest ConditionTest MethodASAHI JAPAN/4013A
Shrinkage rateASTM D9551.8-2.2 %
densityASTM D792/ISO 11831.42
melt mass-flow rateASTM D1238/ISO 113310 g/10min
Water absorption rateASTM D570/ISO 620.2 %
physical property Test ConditionTest MethodASAHI JAPAN/4013A
Shrinkage rate垂直方向旭化成法1.8-2.2 %
平行方向旭化成法1.8-2.2 %
Water absorption rateASTM D5700.2 %
Thermal performanceTest ConditionTest MethodASAHI JAPAN/4013A
melt mass-flow rateASTM D123810 g/10min
Heat distortion temperature0.45MPa，HDTASTM D648172 °C
HDTASTM D648/ISO 75172 ℃（℉）
1.82MPa，HDTASTM D648136 °C
Linear coefficient of thermal expansionTMA法10