PA6 Plaslube® PA6 TL10 Techmer Polymer Modifiers
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Techmer Polymer Modifiers/Plaslube® PA6 TL10 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,3.18mm | ASTM D256 | 48 J/m |
| hardness | Test Condition | Test Method | Techmer Polymer Modifiers/Plaslube® PA6 TL10 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 116 |
| Mechanical properties | Test Condition | Test Method | Techmer Polymer Modifiers/Plaslube® PA6 TL10 |
|---|---|---|---|
| coefficient of friction | 与钢-静态6 | ASTM D1894 | 0.14 |
| elongation | 断裂 | ASTM D638 | 9.5 % |
| tensile strength | 断裂 | ASTM D638 | 64.8 MPa |
| Flexural modulus | ASTM D790 | 2690 MPa | |
| coefficient of friction | 与钢-动态 | ASTM D1894 | 0.20 |
| bending strength | ASTM D790 | 82.7 MPa | |
| Wear factor | ASTM D3702 | 100 10^-8mm³/N·m |
| Electrical performance | Test Condition | Test Method | Techmer Polymer Modifiers/Plaslube® PA6 TL10 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1E+14 ohms·cm | |
| dielectric strength | ASTM D149 | 20 kV/mm |
| physical property | Test Condition | Test Method | Techmer Polymer Modifiers/Plaslube® PA6 TL10 |
|---|---|---|---|
| Water absorption rate | 24hr | ASTM D570 | 1.0 % |
| density | ASTM D792 | 1.20 g/cm³ | |
| Shrinkage rate | MD：3.18mm | ASTM D955 | 1.7 % |
| Thermal performance | Test Condition | Test Method | Techmer Polymer Modifiers/Plaslube® PA6 TL10 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 76.7 °C |
| 0.45MPa,未退火，HDT | ASTM D648 | 160 °C | |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 8.5E-05 cm/cm/°C |