Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC DMX9455-BK1D046 SABIC INNOVATIVE US
LEXAN™
Bottle cap、Electrical field、Electronic field、Automotive sector、Fitness equipment
Scratch resistant、copolymer、wear resistant、Flame retardant、transparent
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/DMX9455-BK1D046 |
|---|---|---|---|
| Total energy at 23 ℃ (73 ℉) | ASTM D3763 | 30 | |
| Impact strength of cantilever beam gap | 23℃ | ASTM D256 | 30 J/m |
| 80*10*3，30℃ | ISO 180/1A | 4 kJ/m² | |
| Suspended wall beam without notch impact strength | 23℃ | ASTM D4812 | NB J/m |
| 80*10*3，23℃ | ISO 180/1U | NB kJ/m² | |
| Charpy Notched Impact Strength | V-notch Edgew 80*10*3 sp=62mm，23℃ | ISO 179/1eA | 3 kJ/m² |
| Impact strength of cantilever beam gap | 80*10*3，23℃ | ISO 180/1A | 5 kJ/m² |
| Charpy Notched Impact Strength | V-notch Edgew 80*10*3 sp=62mm，-30℃ | ISO 179/1eA | 3 kJ/m² |
| Impact strength of cantilever beam gap | 30℃ | ASTM D256 | 30 J/m |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/DMX9455-BK1D046 |
|---|---|---|---|
| Fracture (brk) | Type I, 50 mm/min | ASTM D638 | 65 Mpa |
| Tensile modulus | 1 mm/min | ISO 527 | 2450 Mpa |
| Yield (yld) | 50 mm/min，屈服 | ISO 527 | 7 % |
| 1.3 mm/min, 50 mm span，屈服 | ASTM D790 | 120 Mpa | |
| Flexural modulus | 1.3 mm/min, 50 mm span | ASTM D790 | 2600 Mpa |
| Fracture (brk) | Type I, 50 mm/min | ASTM D638 | 70 % |
| Yield (yld) | 2 mm/min，屈服 | ISO 178 | 108 Mpa |
| Fracture (brk) | 50 mm/min | ISO 527 | 60 Mpa |
| Yield (yld) | Type I, 50 mm/min，屈服 | ASTM D638 | 80 Mpa |
| Fracture (brk) | 50 mm/min | ISO 527 | 40 % |
| Yield (yld) | Type I, 50 mm/min，屈服 | ASTM D638 | 7 % |
| Flexural modulus | 2 mm/min | ISO 178 | 2450 Mpa |
| Tensile modulus | 50 mm/min | ASTM D638 | 2900 Mpa |
| Yield (yld) | 50 mm/min，屈服 | ISO 527 | 80 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/DMX9455-BK1D046 |
|---|---|---|---|
| Water absorption rate | equilibrium, 23C | ASTM D570 | 0.28 % |
| wear resistance | Internal | 10 | |
| Vertical (Flow) | 3.2 mm | Internal | 0.5-0.8 % |
| Water absorption rate | 23°C/sat | ISO 62 | 0.27 % |
| melt mass-flow rate | 300℃/1.2 kg | ASTM D1238 | 14.5 |
| specific volume | ASTM D792 | 0.85 | |
| Melt volume flow rate | ISO 1133 | 13 | |
| Water absorption rate | 24 hours | ASTM D570 | 0.08 % |
| 23°C / 50% RH | ISO 62 | 0.13 % | |
| 50% RH, 24 hrs | ASTM D 570 | 0.04 % | |
| wear resistance | ASTM D 1044 | 10 | |
| Water absorption rate | 50% RH, equilib | ASTM D570 | 0.13 % |