Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 123R-BK1D971 SABIC INNOVATIVE SHANGHAI
LEXAN™ 
Electronic and electrical、Automotive Applications
Low viscosity、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/123R-BK1D971
Suspended wall beam without notch impact strength23°CASTM D48123200 J/m
Impact strength of cantilever beam gapASTM D1822546 kJ/m²
Dart impact23°CASTM D3029169 J
hardnessTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/123R-BK1D971
Rockwell hardnessM 级ASTM D78570
R 级ASTM D785118
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/123R-BK1D971
elongation断裂ASTM D638110 %
屈服ASTM D6387.0 %
Taber abraser1000 Cycles, 1000 g, CS-17 转轮ASTM D104410.0 mg
bending strength屈服, 50.0 mm 跨距ASTM D79093.0 Mpa
tensile strength 断裂ASTM D63865.0 Mpa
屈服ASTM D63862.0 Mpa
Flexural modulus50.0 mm 跨距ASTM D7902340 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/123R-BK1D971
Volume resistivityASTM D257> 1.0E+17 ohms·cm
dielectric constant60 HzASTM D1503.17
Dissipation Factor60 HzASTM D1509.0E-4
50 HzASTM D1509.0E-4
dielectric constant1 MHzASTM D1502.96
Hot wire ignition (HWI)UL 746PLC 4
dielectric strength3.20 mm, in AirASTM D14915 KV/mm
High Voltage Arc Traceability Rate (HVTR)UL 746PLC 2
Compared to the Leakage Tracking Index (CTI)UL 746PLC 2
Dissipation Factor1 MHzASTM D1500.010
High arc combustion index (HAI)UL 746PLC 1
dielectric constant50 kHzASTM D1503.17
optical performance Test ConditionTest MethodSABIC INNOVATIVE SHANGHAI/123R-BK1D971
refractive indexASTM D5421.586
transmissivity2540 µmASTM D100388.0 %
Haze ratio2540 µmASTM D10031.0 %
flammabilityTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/123R-BK1D971
UL flame retardant rating0.76 mmUL 94HB
physical property Test ConditionTest MethodSABIC INNOVATIVE SHANGHAI/123R-BK1D971
Water absorption rate平衡, 23°CASTM D5700.35 %
平衡, 100°CASTM D5700.58 %
Outdoor applicabilityUL 746Cf1
Water absorption rate24 hrASTM D5700.15 %
Specific volumeASTM D7920.830 cm³/g
melt mass-flow rate300°C/1.2 kgASTM D123818 g/10 min
Shrinkage rate3.20 mm，Flow内部方法0.50 - 0.70 %
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/123R-BK1D971
thermal conductivityASTM C1770.19 W/m/K
vicatASTM D15255154 °C
Linear coefficient of thermal expansion-40 到 95°C，流动ASTM E8316.8E-5 cm/cm/°C
specific heatASTM C3511260 J/kg/°C
Heat distortion temperature1.8 MPa, 未退火, 6.40 mm，HDTASTM D648132 °C
RTI ImpUL 746130 °C
RTIUL 746130 °C
Heat distortion temperature0.45 MPa, 未退火, 6.40 mm，HDTASTM D648137 °C
RTI ElecUL 746130 °C
injectionTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/123R-BK1D971
screw speed40 to 70 rpm
Suggested maximum moisture content0.020 %
Processing (melt) temperature280 to 305 °C
drying temperature120 °C
Suggested injection volume40 to 60 %
drying time3.0 to 4.0 hr
Temperature in the middle of the barrel270 to 295 °C
Temperature at the rear of the barrel260 to 280 °C
Exhaust hole depth0.025 to 0.076 mm
Temperature at the front of the material cylinder280 to 305 °C
Back pressure0.300 to 0.700 Mpa
Temperature70 to 95 °C
Spray nozzle temperature275 to 300 °C