PC 141R-111 SABIC INNOVATIVE SHANGHAI
LEXAN™
--
transparent、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/141R-111 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23℃ | ASTM D256 | 801 J/m |
| Suspended wall beam without notch impact strength | /，23℃ | ASTM D4812 | 3204 J/m |
| Instrumented dart impact energy 23 ℃ (73 ℉) total energy | / | ASTM D3763 | 63 J |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/141R-111 |
|---|---|---|---|
| Hardness (Rockwell M) | ASTM D 785 | 70 M | |
| Hardness (Rockwell R) | ASTM D 785 | 118 R |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/141R-111 |
|---|---|---|---|
| elongation at break | Type I, 5 | ASTM D638 | 130 % |
| tensile strength | Type I, 5，断裂 | ASTM D638 | 68 Mpa |
| Flexural modulus | 1.3 mm/ | ASTM D790 | 2340 Mpa |
| elongation | Type I, 5，屈服 | ASTM D638 | 7 % |
| bending strength | 1.3 mm/min/，屈服 | ASTM D790 | 96 Mpa |
| tensile strength | Type I, 5，屈服 | ASTM D638 | 62 Mpa |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/141R-111 |
|---|---|---|---|
| transmittance | 2.54 mm | ASTM D1003 | 88 % |
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/141R-111 |
|---|---|---|---|
| RTI Imp | UL 746B | 130 °C | |
| vicat | Rate B/50 | ASTM D1525 | 154 °C |
| RTI Elec | UL 746B | 130 °C |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/141R-111 |
|---|---|---|---|
| Water absorption rate | 24 hours | ASTM D570 | 0.15 |
| equilibriu | ASTM D570 | 0.35 | |
| melt mass-flow rate | /，300℃/1.2 kg | ASTM D1238 | 10.5 g/10min |
| Shrinkage rate | flow, 3.2 | Internal | 0.5-0.7 |
| specific volume | / | ASTM D792 | 0.83 |