Product Name
Brand Name
Usages
Properties
Certificates
PC HF500R-739 SABIC INNOVATIVE US
LEXAN™
--
enhance、Glass fiber reinforced、Filler: Glass fiber reinf、9.0% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/HF500R-739 |
|---|---|---|---|
| Thermal Conductivity | ISO8302 | 0.21 W/m/K | |
| RTIElec | UL746 | 130 °C | |
| Ball PressureTest | 125°C | IEC60695-10-2 | Pass |
| RTI | UL746 | 125 °C | |
| 0.45MPa, Unannealed,100mm Span | ISO75-2/Be | 140 °C | |
| Linear thermal expansion coefficient | MD：23到80°C | ISO11359-2 | 4E-05 cm/cm/°C |
| Evolution Calendar intelligent importer | UL746 | 125 °C | |
| 1.8MPa, Unannealed,100mm Span | ISO75-2/Ae | 132 °C |
| Hardness | Test Condition | Test Method | SABIC INNOVATIVE US/HF500R-739 |
|---|---|---|---|
| Ball Indentation Hardness | H358/30 | ISO2039-1 | 115 Mpa |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/HF500R-739 |
|---|---|---|---|
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.13 % |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 16.0 cm3/10min |
| Modeling Shrinkage | MD1 | 内部方法 | 0.20到0.60 % |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.31 % |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/HF500R-739 |
|---|---|---|---|
| Flexural Modulus | ISO178 | 3400 Mpa | |
| Taber Abrasion Resistance | 1000Cycles,1000g,CS-17转轮 | 内部方法 | 11.0 mg |
| Tensile Strain | 断裂 | ISO527-2/5 | 7.0 % |
| Tensile Modulus | ISO527-2/1 | 3300 Mpa | |
| Flexural Stress | ISO178 | 95.0 Mpa | |
| Tensile Stress | 断裂 | ISO527-2/5 | 45.0 Mpa |
| Tensile Strain | 屈服 | ISO527-2/5 | 5.0 % |
| Tensile Stress | 屈服 | ISO527-2/5 | 60.0 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/HF500R-739 |
|---|---|---|---|
| Notched Izod Impact Strength | -30°C | ISO180/1A | 7.0 kJ/m² |
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 无断裂 |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 7.0 kJ/m² |
| 23°C | ISO179/1eA | 8.0 kJ/m² | |
| Unnotched Izod Impact Strength | -30°C | ISO180/1U | 110 kJ/m² |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 无断裂 |
| Unnotched Izod Impact Strength | 23°C | ISO180/1U | 无断裂 |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 8.0 kJ/m² |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/HF500R-739 |
|---|---|---|---|
| Glow Wire Flammability Index | 1.00mm | IEC60695-2-12 | 960 °C |
| Oxygen Index | ISO4589-2 | 35 % | |
| Flame Rating | 1.50mm | UL94 | V-0 |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/HF500R-739 |
|---|---|---|---|
| Dielectric Strength | 3.20mm,在油中 | IEC60243-1 | 16 KV/mm |
| 1.60mm,在油中 | IEC60243-1 | 25 KV/mm | |
| Volume Resistivity | IEC60093 | >1.0E+15 ohms·cm | |
| Comparative Tracking Index | IEC60112 | 175 V | |
| Dielectric Strength | 0.800mm,在油中 | IEC60243-1 | 33 KV/mm |
| Dissipation Factor? | 60Hz | IEC60250 | 1E-03 |
| Surface Resistivity | IEC60093 | >1.0E+15 ohms | |
| Relative Permittivity | 60Hz | IEC60250 | 2.90 |
| 1MHz | IEC60250 | 2.80 | |
| Dissipation Factor? | 50Hz | IEC60250 | 1E-03 |
| Relative Permittivity | 50Hz | IEC60250 | 2.90 |
| Dissipation Factor? | 1MHz | IEC60250 | 0.010 |