PBT+ASA SCANBLEND P AP2060 F30B POLYKEMI SWEDEN
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | POLYKEMI SWEDEN/SCANBLEND P AP2060 F30B |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 10 kJ/m² |
| -30°C | ISO 179 | 8.0 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179 | 60 kJ/m² |
| 23°C | ISO 179 | 48 kJ/m² |
| Mechanical properties | Test Condition | Test Method | POLYKEMI SWEDEN/SCANBLEND P AP2060 F30B |
|---|---|---|---|
| Flexural modulus | 23°C | ISO 178 | 9800 MPa |
| tensile strength | ISO 527-2 | 114 MPa | |
| Tensile strain | 断裂 | ISO 527-2 | 8.0 % |
| 屈服 | ISO 527-2 | 7.0 % | |
| bending strength | ISO 178 | 184 MPa |
| flammability | Test Condition | Test Method | POLYKEMI SWEDEN/SCANBLEND P AP2060 F30B |
|---|---|---|---|
| Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | 750 °C |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | POLYKEMI SWEDEN/SCANBLEND P AP2060 F30B |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 0.60to0.80 % |
| MD | ISO 294-4 | 0.10to0.30 % | |
| density | ISO 1183 | 1.48 g/cm³ | |
| melt mass-flow rate | 275°C/2.16kg | ISO 1133 | 12 g/10min |
| Thermal performance | Test Condition | Test Method | POLYKEMI SWEDEN/SCANBLEND P AP2060 F30B |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 215 °C |
| vicat | -- | ISO 306/A50 | 215 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 195 °C |
| vicat | -- | ISO 306/B50 | 185 °C |