PC URZ2500 IDEMITSU JAPAN
TARFLON™
Automotive Applications、Home appliance components
Flame retardant、UV resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | IDEMITSU JAPAN/URZ2500 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 15 kJ/m² |
| Mechanical properties | Test Condition | Test Method | IDEMITSU JAPAN/URZ2500 |
|---|---|---|---|
| Nominal tensile fracture strain | ISO 527-2 | 60 % | |
| bending strength | ISO 178 | 90.0 Mpa | |
| Flexural modulus | ISO 178 | 2600 Mpa | |
| tensile strength | 屈服 | ISO 527-2 | 60.0 Mpa |
| optical performance | Test Condition | Test Method | IDEMITSU JAPAN/URZ2500 |
|---|---|---|---|
| ISO 9660 | >PC-MD10FR(40)< | ||
| transmissivity | 1000 µm | ISO 13468-1 | 0.6 % |
| reflectivity | 97.0 |
| flammability | Test Condition | Test Method | IDEMITSU JAPAN/URZ2500 |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | IDEMITSU JAPAN/URZ2500 |
|---|---|---|---|
| Shrinkage rate | 横向流量 : 2.00 mm | 内部方法 | 0.50 - 0.70 % |
| Melt volume flow rate | 300°C/1.2 kg | ISO 1133 | 42.0 cm3/10min |
| Shrinkage rate | 流量 : 2.00 mm | 内部方法 | 0.50 - 0.70 % |
| density | ISO 1183 | 1.28 g/cm³ |
| Thermal performance | Test Condition | Test Method | IDEMITSU JAPAN/URZ2500 |
|---|---|---|---|
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 127 °C |
| 1.8 MPa, 未退火，HDT | ISO 75-2/A | 117 °C | |
| RTI Imp | UL 746 | 80.0 °C | |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 6.5E-5 cm/cm/°C |
| RTI | UL 746 | 80.0 °C | |
| RTI Elec | UL 746 | 80.0 °C |
| injection | Test Condition | Test Method | IDEMITSU JAPAN/URZ2500 |
|---|---|---|---|
| drying time | 5.0 to 8.0 hr | ||
| Temperature in the middle of the barrel | 260 to 280 °C | ||
| Temperature at the rear of the barrel | 260 to 280 °C | ||
| drying temperature | 120 °C | ||
| Temperature at the front of the material cylinder | 260 to 280 °C | ||
| Temperature | 80 to 90 °C |