PC URC2500 IDEMITSU JAPAN
TARFLON™
Lighting diffuser
Flame retardant,High reflectivity
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
thermal performance | Test Condition | Test Method | IDEMITSU JAPAN/URC2500 |
---|---|---|---|
Hot deformation temperature | 0.45 MPa, Unannealed | ISO 75-2/B | 138 °C |
1.8 MPa, Unannealed | ISO 75-2/A | 126 °C | |
Linear coefficient of thermal expansion | Flow | ISO 11359-2 | 6.5E-5 cm/cm/°C |
RTI | UL 746 | 80.0 °C | |
RTI Elec | UL 746 | 80.0 °C | |
RTI Imp | UL 746 | 80.0 °C |
mechanical properties | Test Condition | Test Method | IDEMITSU JAPAN/URC2500 |
---|---|---|---|
Bending modulus | ISO 178 | 2400 Mpa | |
bending strength | ISO 178 | 90.0 Mpa | |
Nominal tensile fracture strain | ISO 527-2 | 70 % | |
tensile strength | Yield | ISO 527-2 | 60.0 Mpa |
Physical properties | Test Condition | Test Method | IDEMITSU JAPAN/URC2500 |
---|---|---|---|
density | ISO 1183 | 1.28 g/cm³ | |
Melt Volume Flow Rate (MVR) | 300°C/1.2 kg | ISO 1133 | 28.0 cm3/10min |
Shrinkage rate | Flow : 2.00 mm | Internal Method | 0.50 - 0.70 % |
横向Flow : 2.00 mm | Internal Method | 0.50 - 0.70 % |
impact performance | Test Condition | Test Method | IDEMITSU JAPAN/URC2500 |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179 | 40 kJ/m² |
flammability | Test Condition | Test Method | IDEMITSU JAPAN/URC2500 |
---|---|---|---|
UL flame retardant rating | 1.5 mm | UL 94 | V-0 |
optical performance | Test Condition | Test Method | IDEMITSU JAPAN/URC2500 |
---|---|---|---|
ISO | PC-MD10 | ||
reflectivity | 97.0 | ||
transmissivity | 1000 μm | ISO 13468-1 | 0.6 % |
injection | Test Condition | Test Method | IDEMITSU JAPAN/URC2500 |
---|---|---|---|
drying temperature | 120 °C | ||
drying time | 5.0 to 8.0 hr | ||
Mold temperature | 80 to 90 °C | ||
Temperature at the front of the material cylinder | 260 to 280 °C | ||
Temperature at the rear of the barrel | 260 to 280 °C | ||
Temperature in the middle of the barrel | 260 to 280 °C |