Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM MG210 ASAHI JAPAN
TENAC™
Engine parts,Engineering accessories,Shell,Conveyor accessories,Fasteners,Automotive sector,bearing,Engineering accessories,Engine parts,Fasteners,Shell,bearing,Conveyor accessories,Application in the automotive field
high viscosity,High toughness,Fatigue resistance,Creep resistance,High impact resistance,high strength,High rigidity,Dimensional stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | ASAHI JAPAN/MG210 |
|---|---|---|---|
| Rockwell hardness | M级 | ASTM D785 | 94 |
| R级 | ASTM D785 | 120 |
| Electrical performance | Test Condition | Test Method | ASAHI JAPAN/MG210 |
|---|---|---|---|
| dielectric constant | 23°C,1MHz | ASTM D150 | 3.80 |
| Surface Resistivity | ASTM D257 | 1.0E+16-1.0E+17 ohms | |
| Volume resistivity | 23°C | ASTM D257 | 1.0E+15-1.0E+16 ohms·cm |
| Dissipation Factor | 23°C,1MHz | ASTM D150 | 7E-03 |
| dielectric strength | ASTM D149 | 18 KV/mm | |
| arc resistance | ASTM D495 | 250 sec |
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/MG210 |
|---|---|---|---|
| Taber abraser | ASTM D1044 | 13.0 mg | |
| Tensile modulus | ISO 527-2 | 3150 Mpa | |
| elongation | 断裂 | ASTMD638 | 40 % |
| tensile strength | -- | ASTM D638 | 79.0 Mpa |
| bending strength | ASTM D790 | 108 Mpa | |
| Flexural modulus | -- | ISO 178 | 2900 Mpa |
| tensile strength | 屈服 | ISO 527-2 | 75.0 Mpa |
| Flexural modulus | -- | ASTM D790 | 3040 Mpa |
| physical property | Test Condition | Test Method | ASAHI JAPAN/MG210 |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 1.8-2.2 % |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 1.7 g/10min |
| Water absorption rate | 23°C,24hr,50%RH | ASTM D570 | 0.20 % |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/MG210 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 136 °C |
| 0.45MPa,未退火，HDT | ASTM D648 | 172 °C | |
| thermal conductivity | 0.23 W/m/K | ||
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 167 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 103 °C | |
| specific heat | 1470 J/kg/°C | ||
| Linear coefficient of thermal expansion | MD | ASTMD696 | 1E-04 cm/cm/°C |