Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS HI-12 INEOS STYRO KOREA
Terluran®
Household goods、Electronic field、Helmet、Electrical appliances、Electrical/Electronic App
High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | INEOS STYRO KOREA/HI-12 |
|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C | ISO180/A | 11 kJ/m² |
| 23°C | ISO180/A | 31 kJ/m² | |
| Charpy Notched Impact Strength | -30°C | ISO179 | 11 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179 | 无断裂 |
| -30°C | ISO179 | 160 kJ/m² | |
| Impact strength of cantilever beam gap | 23°C | ASTMD256 | 35.0 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179 | 30 kJ/m² |
| hardness | Test Condition | Test Method | INEOS STYRO KOREA/HI-12 |
|---|---|---|---|
| ISO2039-1 | 80.0 Mpa | ||
| Rockwell hardness | R计秤 | ISO2039-2 | 101 |
| Mechanical properties | Test Condition | Test Method | INEOS STYRO KOREA/HI-12 |
|---|---|---|---|
| Tensile strain | 屈服,23°C | ISO527-2 | 2.7 % |
| Bending stress | ISO178 | 58.0 Mpa | |
| Tensile modulus | ISO527-2 | 1900 Mpa | |
| Tensile stress | 屈服,23°C | ISO527-2 | 40.0 Mpa |
| Electrical performance | Test Condition | Test Method | INEOS STYRO KOREA/HI-12 |
|---|---|---|---|
| Dissipation Factor | 1MHz | IEC60250 | 8.2E-03 |
| CTI | IEC60112 | 600 V | |
| dielectric constant | 1.00mm,1MHz | 2.80 | |
| Volume resistivity | IEC60093 | 1E+15 ohms·cm | |
| dielectric constant | 100Hz | IEC60250 | 2.90 |
| Dissipation Factor | 100Hz | IEC60250 | 5.4E-03 |
| flammability | Test Condition | Test Method | INEOS STYRO KOREA/HI-12 |
|---|---|---|---|
| UL flame retardant rating | 3.2mm | UL94 | HB |
| 1.6mm | UL94 | HB |
| physical property | Test Condition | Test Method | INEOS STYRO KOREA/HI-12 |
|---|---|---|---|
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 0.21 % |
| 饱和,23°C | ISO62 | 1.0 % | |
| density | ISO1183 | 1.02 g/cm³ | |
| Melt volume flow rate | 220°C/10.0kg | ISO1133 | 14.0 cm3/10min |
| Shrinkage rate | ISO294-4 | 0.40到0.70 % |
| Thermal performance | Test Condition | Test Method | INEOS STYRO KOREA/HI-12 |
|---|---|---|---|
| thermal conductivity | DIN52612 | 0.17 W/m/K | |
| vicat | -- | ISO306/A50 | 104 °C |
| Hot deformation temperature 3 | 1.8MPa,退火 | ISO75-2/A | 97.0 °C |
| MD | ISO11359-2 | 8.0E-5到1.1E-4 cm/cm/°C | |
| Hot deformation temperature 3 | 0.45MPa,退火 | ISO75-2/B | 102 °C |
| vicat | -- | ISO306/B50 | 96.0 °C |
| maximum service temperature | 80 °C |