Polyarylate U-polymer P-1001 UNITIKA JAPAN
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | UNITIKA JAPAN/U-polymer P-1001 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,3.18mm | ASTM D256 | 260 J/m |
| hardness | Test Condition | Test Method | UNITIKA JAPAN/U-polymer P-1001 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 123 |
| Mechanical properties | Test Condition | Test Method | UNITIKA JAPAN/U-polymer P-1001 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 65 % |
| tensile strength | ASTM D638 | 69.0 MPa | |
| compressive strength | ASTM D695 | 81.0 MPa | |
| Flexural modulus | ASTM D790 | 2100 MPa | |
| bending strength | ASTM D790 | 82.0 MPa |
| Electrical performance | Test Condition | Test Method | UNITIKA JAPAN/U-polymer P-1001 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 2E+16 ohms·cm | |
| dielectric strength | ASTM D149 | 31 kV/mm | |
| Dissipation Factor | 1MHz | ASTM D150 | 0.010 |
| dielectric constant | 1MHz | ASTM D150 | 3.00 |
| arc resistance | ASTM D495 | 127 sec |
| optical performance | Test Condition | Test Method | UNITIKA JAPAN/U-polymer P-1001 |
|---|---|---|---|
| transmissivity | 3000µm | ASTM D1003 | 87.0 % |
| physical property | Test Condition | Test Method | UNITIKA JAPAN/U-polymer P-1001 |
|---|---|---|---|
| Shrinkage rate | MD：3.00mm | ASTM D955 | 0.80 % |
| Water absorption rate | 24hr,3.18mm | ASTM D570 | 0.26 % |
| density | ASTM D792 | 1.21 g/cm³ |
| Thermal performance | Test Condition | Test Method | UNITIKA JAPAN/U-polymer P-1001 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 175 °C |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 6.2E-05 cm/cm/°C |