UHMWPE L5000 MITSUI CHEM JAPAN
LUBMER™
Engine parts、Automotive interior parts、Thin walled components、bearing
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | MITSUI CHEM JAPAN/L5000 |
|---|---|---|---|
| NotchedIzodImpact | 23°C,2.00mm | ASTMD256 | 190 J/m |
| hardness | Test Condition | Test Method | MITSUI CHEM JAPAN/L5000 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTMD785 | 51 |
| Electrical performance | Test Condition | Test Method | MITSUI CHEM JAPAN/L5000 |
|---|---|---|---|
| Volume resistivity | ASTMD257 | 1E+17 ohms·cm | |
| Dissipation Factor | 1MHz | ASTMD150 | 1E-04 |
| dielectric strength | ASTMD149 | 44 KV/mm | |
| dielectric constant | 23°C | ASTMD150 | 2.40 |
| Mechanical properties | Test Condition | Test Method | MITSUI CHEM JAPAN/L5000 |
|---|---|---|---|
| elongation | 断裂,23°C | ASTMD638 | 10 % |
| tensile strength | 断裂,23°C | ASTMD638 | 47.0 Mpa |
| Flexural modulus | 23°C,3.00mm,48.0mmSpan | ASTMD790 | 1620 Mpa |
| Flexural Strength3 | Yield,23°C,3.00mm,48.0mmSpan | ASTMD790 | 38.0 Mpa |
| flammability | Test Condition | Test Method | MITSUI CHEM JAPAN/L5000 |
|---|---|---|---|
| FlameRating | 1.6mm | UL94 | HB |
| physical property | Test Condition | Test Method | MITSUI CHEM JAPAN/L5000 |
|---|---|---|---|
| Shrinkage rate | TD：2.00mm | ASTMD955 | 1.6 % |
| Water absorption rate | 24hr | ASTMD570 | 0.010 % |
| Shrinkage rate | MD：2.00mm | ASTMD955 | 1.8 % |
| Thermal performance | Test Condition | Test Method | MITSUI CHEM JAPAN/L5000 |
|---|---|---|---|
| MD | ASTMD696 | 1.3E-04 cm/cm/°C | |
| 0.45MPa,未退火 | ASTMD648 | 80.0 °C | |
| vicat | ASTMD15254 | 130 °C |