ABS Lastilac AR-V0E LATI S.p.A.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LATI S.p.A./Lastilac AR-V0E |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 7.0 kJ/m² |
| -20°C | ISO 179/1eA | 4.0 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 50 kJ/m² |
| -20°C | ISO 179/1eU | 35 kJ/m² |
| Supplementary Information | Test Condition | Test Method | LATI S.p.A./Lastilac AR-V0E |
|---|---|---|---|
| dimensional stability | 79.0 |
| Mechanical properties | Test Condition | Test Method | LATI S.p.A./Lastilac AR-V0E |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 8.0 % |
| tensile strength | 断裂,90°C | ISO 527-2/5 | 5.00 MPa |
| Tensile strain | 屈服,60°C | ISO 527-2/5 | 2.3 % |
| tensile strength | 屈服,90°C | ISO 527-2/5 | 20.0 MPa |
| 屈服,60°C | ISO 527-2/5 | 30.0 MPa | |
| Tensile modulus | 90°C | ISO 527-2/1 | 1500 MPa |
| 23°C | ISO 527-2/1 | 2300 MPa | |
| 60°C | ISO 527-2/1 | 1900 MPa | |
| tensile strength | 断裂,60°C | ISO 527-2/5 | 20.0 MPa |
| 屈服,23°C | ISO 527-2/5 | 40.0 MPa | |
| 断裂,23°C | ISO 527-2/5 | 35.0 MPa | |
| Tensile strain | 屈服,90°C | ISO 527-2/5 | 2.3 % |
| 断裂,60°C | ISO 527-2/5 | 50 % | |
| 断裂,90°C | ISO 527-2/5 | 95 % | |
| 屈服,23°C | ISO 527-2/5 | 2.0 % |
| Electrical performance | Test Condition | Test Method | LATI S.p.A./Lastilac AR-V0E |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 2 |
| flammability | Test Condition | Test Method | LATI S.p.A./Lastilac AR-V0E |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-2 |
| Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | 725 °C |
| UL flame retardant rating | 3.0mm | UL 94 | V-0 |
| Hot filament ignition temperature | 1.0mm | IEC 60695-2-13 | 850 °C |
| Burning wire flammability index | 1.0mm | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 960 °C |
| Limiting Oxygen Index | ASTM D2863 | 28 % |
| physical property | Test Condition | Test Method | LATI S.p.A./Lastilac AR-V0E |
|---|---|---|---|
| Shrinkage rate | MD:2.00mm | ISO 294-4 | 0.40to0.60 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.040 % |
| density | ISO 1183 | 1.20 g/cm³ | |
| Shrinkage rate | TD:2.00mm | ISO 294-4 | 0.45to0.65 % |
| Thermal performance | Test Condition | Test Method | LATI S.p.A./Lastilac AR-V0E |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 85.0 °C |
| vicat | ISO 306/B50 | 95.0 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 80.0 °C |
| Continuous use temperature | 70.0 °C | ||
| Linear coefficient of thermal expansion | MD：30到100°C | ISO 11359-2 | 3.5E-05 cm/cm/°C |