Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM CE66 CELANESE GERMANY
HOSTAFORM®
Automotive sector
High impact resistance、wear resistant、Filler: Glass fiber reinf、25% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | CELANESE GERMANY/CE66 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 8.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | CELANESE GERMANY/CE66 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1A/1 | 8450 Mpa | |
| tensile strength | 断裂 | ISO 527-2/1A/5 | 120 Mpa |
| Tensile strain | 断裂 | ISO 527-2/1A/5 | 2.5 % |
| tensile strength | 断裂,23°C | ASTM D638 | 138 Mpa |
| physical property | Test Condition | Test Method | CELANESE GERMANY/CE66 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.40 % |
| TD | ISO 294-4 | 0.80 % | |
| MD | ISO 294-4 | 0.40 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
| density | ASTM D792 | 1.58 g/cm³ | |
| Shrinkage rate | TD | ASTM D955 | 1.0 % |
| density | ISO 1183 | 1.57 g/cm³ | |
| melt mass-flow rate | ASTM D1238 | 6.5 g/10min | |
| Melt volume flow rate | 250°C/2.16kg | ISO 1133 | 8.50 cm3/10min |
| Thermal performance | Test Condition | Test Method | CELANESE GERMANY/CE66 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 163 °C |
| melting temperature | ISO 11357-3 | 166 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 160 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 2.7E-05 cm/cm/°C |
| TD | ISO 11359-2 | 1.3E-04 cm/cm/°C |