Certificates
POM KFL-4416 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Casters、household electrical appl
High temperature resistan、UV resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/KFL-4416 |
|---|---|---|---|
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 132 °C |
| 0.45 MPa, 未退火, 3.20 mm | 161 °C | ||
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 3 | ISO 75-2/Af | 147 °C |
| Injection | Test Condition | Test Method | SABIC INNOVATIVE US/KFL-4416 |
|---|---|---|---|
| Middle Temperature | 195 到 205 °C | ||
| Processing (Melt) Temp | 200 到 215 °C | ||
| Drying Time | 4.0 hr | ||
| Rear Temperature | 175 到 190 °C | ||
| Drying Temperature | 80 °C | ||
| Front Temperature | 210 到 220 °C | ||
| Back Pressure | 0.200 到 0.300 Mpa | ||
| Mold Temperature | 80 到 110 °C | ||
| Screw Speed | 30 到 60 rpm |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/KFL-4416 |
|---|---|---|---|
| Modeling Shrinkage | 流动 : 24小时 | ASTM D955 | 1.4 % |
| Moisture Absorption | 24 hr, 50% RH | ASTM D570 | 0.16 % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.29 % | |
| Modeling Shrinkage | 横向流动 : 24小时 | ASTM D955 | 1.6 % |
| 横向流量 : 24小时 | ISO 294-4 | 1.3 % | |
| 流量 : 24小时 | 1.5 % |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/KFL-4416 |
|---|---|---|---|
| Tensile Elongation | 屈服 | ISO 527-2 | 2.3 % |
| Tensile Modulus | -- | ISO 527-2/1 | 5800 Mpa |
| Flexural Strength | ASTM D790, ISO 178 | 92.0 Mpa | |
| Specific Wear Rate | ASTM D3702 | 1.9E+8 10^-8 mm³/N·m | |
| Flexural Modulus | -- | ISO 178 | 6300 Mpa |
| Coefficient of Friction | Dynamic | ASTM D3702 | 0.50 |
| Tensile Strength | 断裂 | ISO 527-2 | 46.0 Mpa |
| ASTM D638 | 56.0 Mpa | ||
| Tensile Elongation | 2.6 % | ||
| Tensile Modulus | -- 1 | 6130 Mpa | |
| Flexural Modulus | -- | ASTM D790 | 5300 Mpa |
| Tensile Elongation | 断裂 | ISO 527-2 | 4.0 % |
| Tensile Strength | 屈服 | ASTM D638 | 56.0 Mpa |
| ISO 527-2 | 49.0 Mpa | ||
| Tensile Elongation | ASTM D638 | 3.6 % | |
| Coefficient of Friction | Static | ASTM D3702 | 0.43 |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/KFL-4416 |
|---|---|---|---|
| Unnotched Izod Impact Strength | 23°C | ASTM D4812 | 210 J/m |
| 23°C 3 | ISO 180/1U | 17 kJ/m² | |
| Instrumented Dart Impact | 23°C, Energy at Peak | ASTM D3763 | 9.00 J |
| -- | ISO 6603-2 | 2.00 J |