PA66 3101T-30V TORAY JAPAN
Amilan®
Electrical appliances,Electronic and Electrical Applications
enhance,Conductive,Filler: Carbon fiber rein,30%,Filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/3101T-30V |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2 | 1.6 % |
| bending strength | 23°C | ISO 178 | 335 Mpa |
| Flexural modulus | 23°C | ISO 178 | 19000 Mpa |
| AmountofWear-vs.S45C | SuzukiMethod | 0.600 mg/hr | |
| Friction coefficient - vs.S45C | SuzukiMethod | 0.23 | |
| tensile strength | 23°C | ISO 527-2 | 240 Mpa |
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/3101T-30V |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 2.0 ohms·cm |
| flammability | Test Condition | Test Method | TORAY JAPAN/3101T-30V |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | TORAY JAPAN/3101T-30V |
|---|---|---|---|
| Shrinkage rate | MD:3.00mm4 | 内部方法 | 0.20 % |
| PVLimit-vs.S45C | SuzukiMethod | 2.6 MPa·m/s | |
| Shrinkage rate | 吸水率(平衡,23°C,50%RH) | 内部方法 | 1.8 % |
| TD:3.00mm3 | 内部方法 | 0.60 % |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/3101T-30V |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 250 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 2E-05 cm/cm/°C |
| melting temperature | DSC | 265 °C |