PPS TS201HS TOYOBO JAPAN
--
--
dimensional stability 、High rigidity、Filler: Glass mineral
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | TOYOBO JAPAN/TS201HS |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 121 |
| Mechanical properties | Test Condition | Test Method | TOYOBO JAPAN/TS201HS |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 2650 kg/cm²(MPa)[Lb/in²] | |
| Tensile modulus | ASTM D638 | 21600 Mpa | |
| elongation | 断裂 | ASTM D638 | 1.4 % |
| Flexural modulus | ASTM D790/ISO 178 | 21*10^4 kg/cm²(MPa)[Lb/in²] | |
| bending strength | 屈服 | ASTM D790 | 234 Mpa |
| Tensile modulus | ASTM D638/ISO 527 | 23*10^4 kg/cm²(MPa)[Lb/in²] | |
| tensile strength | 屈服 | ASTM D638 | 170 Mpa |
| Flexural modulus | ASTM D790 | 18600 Mpa | |
| tensile strength | ASTM D638/ISO 527 | 2010 kg/cm²(MPa)[Lb/in²] |
| Electrical performance | Test Condition | Test Method | TOYOBO JAPAN/TS201HS |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
| Dissipation Factor | 1kHz | ASTM D150 | 0.055 |
| Volume resistivity | ASTM D257 | 1E+15 ohms·cm | |
| dielectric constant | 1kHz | ASTM D150 | 5.10 |
| Dissipation Factor | 1MHz | ASTM D150 | 8.5E-03 |
| arc resistance | ISO 14782 | 173 | |
| dielectric strength | ASTM D149 | 11 KV/mm | |
| dielectric constant | 1MHz | ASTM D150 | 4.50 |
| arc resistance | ASTM D495 | 137 sec |
| other | Test Condition | Test Method | TOYOBO JAPAN/TS201HS |
|---|---|---|---|
| characteristic | 玻璃纤维和无机物填充增强等级.与40%玻璃纤维增强等级一样的性能 |
| Physical properties | Test Condition | Test Method | TOYOBO JAPAN/TS201HS |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.96 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.02 % |
| flammability | Test Condition | Test Method | TOYOBO JAPAN/TS201HS |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 |
| physical property | Test Condition | Test Method | TOYOBO JAPAN/TS201HS |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.15 % |
| Water absorption rate | 24hr | ASTM D570 | 0.020 % |
| Shrinkage rate | TD | ASTM D955 | 0.45 % |
| Thermal performance | Test Condition | Test Method | TOYOBO JAPAN/TS201HS |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 260 °C |
| Linear coefficient of thermal expansion | TD | ASTM D696 | 4.8E-05 cm/cm/°C |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | >260 ℃（℉） |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 1.2E-05 cm/cm/°C |