Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC LV-2225Z TEIJIN JAPAN
PANLITE®
Electrical field,Electronic field,currency
Low viscosity,transparent,UV resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodTEIJIN JAPAN/LV-2225Z
Impact strength of simply supported beam without notch23°CISO 179NoBreak
Mechanical propertiesTest ConditionTest MethodTEIJIN JAPAN/LV-2225Z
Tensile modulusISO 527-2/12400 Mpa
bending strengthASTM D790/ISO 178/94 kg/cm²(MPa)[Lb/in²]
Flexural modulusASTM D790/ISO 178/2400 kg/cm²(MPa)[Lb/in²]
Charpy Notched Impact Strength23°CISO 179/1eA71 kJ/m²
elongationASTM D638/ISO 527/6 %
Tensile modulus23°CISO 527-22400 Mpa
Nominal tensile fracture strainISO 527-2/50>50 %
Tensile strain屈服ISO 527-2/506.0 %
tensile strength ASTM D638/ISO 527/61 kg/cm²(MPa)[Lb/in²]
屈服ISO 527-2/5061.0 Mpa
bending strength23°CISO 17894 Mpa
ISO 17894.0 Mpa
Flexural modulusISO 1782400 Mpa
23°CISO 1782400 Mpa
Tensile modulusASTM D638/ISO 527/2400 kg/cm²(MPa)[Lb/in²]
elongation at break23°CISO 527-250 %
tensile strength 23°CISO 527-261 Mpa
Electrical performanceTest ConditionTest MethodTEIJIN JAPAN/LV-2225Z
Compared to the Leakage Tracking Index (CTI)IEC 60112PLC 3
dielectric constant100HzIEC 602503.10
Dissipation Factor相对漏电起痕指数IEC 60112225 V
100HzIEC 602501E-03
dielectric constantASTM D150/IEC 602503
Surface ResistivityIEC 600931E+15 Ω.cm
dielectric constant1MHzIEC 602503.00
Dissipation Factor23°CIEC 602509E-03 1MHz
1MHzIEC 602509E-03
Volume resistivityIEC 600931E+15 Ω.cm
dielectric strengthIEC 60243-130 KV/mm
Volume resistivityIEC 60093>1.0E+15 ohms·cm
dielectric constant23°CIEC 602503.00 1MHz
Surface ResistivityIEC 60093>1.0E+15 ohms
Dissipation Factor23°CIEC 602501E-03 100HZ
optical performance Test ConditionTest MethodTEIJIN JAPAN/LV-2225Z
transmissivity3000µmASTM D100388.0 %
refractive indexISO 4891.59 °C
ASTM D542/ISO 4891.585
ASTM D5421.585
transmittance3000μmISO 13468-288.0 %
ASTM D1003/ISO 1346888 %
Physical propertiesTest ConditionTest MethodTEIJIN JAPAN/LV-2225Z
Shrinkage rateASTM D9550.5-0.7 %
densityASTM D792/ISO 1183/1200
Water absorption rateASTM D570/ISO 620.2 %
flammabilityTest ConditionTest MethodTEIJIN JAPAN/LV-2225Z
Burning wire flammability index3.0mmIEC 60695-2-12960 °C
UL flame retardant rating3.0mmUL 94V-2
Burning wire flammability index1.5mmIEC 60695-2-12850 °C
Hot filament ignition temperature3.0mmIEC 60695-2-13875 °C
UL flame retardant ratingUL -94V-2 1.5mm
UL -94V-2 0.40mm
UL -94V-2 0.75mm
Hot filament ignition temperature1.5mmIEC 60695-2-13850 °C
UL flame retardant rating1.5mmUL 94V-2
0.40mmUL 94V-2
UL -94V-2 3.0mm
UL -94V-2 6.0mm
physical property Test ConditionTest MethodTEIJIN JAPAN/LV-2225Z
Water absorption rate(23°C,24hr)ISO 620.20 %
Shrinkage rateMD2.0mmISO 294-40.60 %
Water absorption rate23°C,24hrISO 620.20 %
Melt volume flow rate300°C/1.2kgISO 113315.0 cm3/10min
Shrinkage rateMD:4.00mm内部方法0.50-0.70 %
melt mass-flow rate300℃/1.2KgISO 113311.0 cm3/10min
Shrinkage rateTD:4.00mm内部方法0.50-0.70 %
TD2.0mmISO 294-40.60 %
Thermal performanceTest ConditionTest MethodTEIJIN JAPAN/LV-2225Z
Heat distortion temperature1.80MPa退火，HDTISO 75-2/Af128 °C
RTI Imp1.5mmUL 746115 °C
vicatASTM D1525/ISO R306148 ℃（℉）
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/B141 °C
vicatISO 306/B50148 °C
Heat distortion temperature1.8MPa,未退火，HDTISO 75-2/A125 °C
RTI Str1.5mmUL 746125 °C
Linear coefficient of thermal expansionMDISO 11359-27E-05 cm/cm/°C
RTI Elec1.5mmUL 746125 °C
Heat distortion temperature0.45MPa未退火，HDTISO 75-2/Bf141 °C
Linear coefficient of thermal expansionTDISO 11359-27E-05 cm/cm/°C
ASTM D696/ISO 113590.7 mm/mm.℃