EMAA Surlyn® 8320 DUPONT USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/Surlyn® 8320 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D1822 | 1270 kJ/m² |
| hardness | Test Condition | Test Method | DUPONT USA/Surlyn® 8320 |
|---|---|---|---|
| Shore hardness | 邵氏D | ASTM D2240 | 36 |
| 邵氏D | ISO 868 | 36 |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/Surlyn® 8320 |
|---|---|---|---|
| tensile strength | 断裂,23°C | ASTM D638 | 18.6 MPa |
| Tensile strain | 断裂,23°C | ISO 527-2 | 560 % |
| wear resistance | NBS指数 | ASTM D1630 | 61.0 |
| Flexural modulus | 23°C | ASTM D790 | 30.3 MPa |
| tensile strength | 断裂,23°C | ISO 527-2 | 18.6 MPa |
| Yield,23°C,CompressionMolded | ASTM D638 | 3.10 MPa | |
| elongation | 断裂,23°C | ASTM D638 | 560 % |
| optical performance | Test Condition | Test Method | DUPONT USA/Surlyn® 8320 |
|---|---|---|---|
| Haze ratio | 6350µm | ASTM D1003 | 27 % |
| physical property | Test Condition | Test Method | DUPONT USA/Surlyn® 8320 |
|---|---|---|---|
| density | ASTM D792 | 0.950 g/cm³ | |
| ISO 1183 | 0.950 g/cm³ | ||
| IonType | Sodium | ||
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 1.0 g/10min |
| 190°C/2.16kg | ISO 1133 | 1.0 g/10min |
| Thermal performance | Test Condition | Test Method | DUPONT USA/Surlyn® 8320 |
|---|---|---|---|
| vicat | ASTM D1525 | 47.0 °C | |
| ISO 306 | 47.0 °C | ||
| melting temperature | ASTM D3418 | 70.0 °C | |
| FreezingPoint | -- | ISO 3146 | 38 °C |
| -- | ASTM D3418 | 38 °C | |
| melting temperature | ISO 3146 | 70.0 °C |